Anti-perspiration sterilizing insole filler powder and preparation method thereof
A technology for filling powder and insole, applied in insoles, footwear, clothing, etc., can solve the problems of undiscovered, complex extraction of Chinese herbal medicine, chemical agent damage to the human body, etc., and achieve the effect of preventing bacterial reproduction and good antibacterial effect.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] Weigh 50 parts of bentonite, 10 parts of Huoxiang, 5 parts of boric acid, and 20 parts of a mixture of citric acid and sodium citrate with a pH value of 5.0, and input them into a mixer for stirring. Grind the powder to get the antiperspirant and antibacterial insole filling powder.
[0020] The content of lead in the bentonite is less than 5 parts per million, the content of cadmium is less than 3 parts per million, the content of arsenic is less than 2 parts per million, the content of mercury is less than 2 parts per million, and the content of copper is less than 2 parts per million 20 / 20.
[0021] The particle fineness after grinding is ≤0.074mm.
[0022] The moisture content after drying is ≤1%.
[0023] The bactericidal effect of the antiperspirant and sterilizing insole filling powder prepared in Table 1 Example 1
[0024] microorganism
Embodiment 2
[0026] Weigh 60 parts of bentonite, 15 parts of mint, 6 parts of citric acid, 30 parts of a mixture of potassium dihydrogen phosphate and disodium hydrogen phosphate with a pH value of 5.5, input them into a mixer for stirring, and dry them after stirring evenly, and then input them into a mill The powder is milled in the machine to obtain the antiperspirant and sterilizing insole filling powder.
[0027] The content of lead in the bentonite is less than 5 parts per million, the content of cadmium is less than 3 parts per million, the content of arsenic is less than 2 parts per million, the content of mercury is less than 2 parts per million, and the content of copper is less than 2 parts per million 20 / 20.
[0028] The particle fineness after grinding is ≤0.074mm.
[0029] The moisture content after drying is ≤1%.
[0030] The bactericidal effect of the antiperspirant and antiseptic insole filling powder that table 2 embodiment 2 makes
[0031] microorganism
Embodiment 3
[0033] Weigh 70 parts of bentonite, 20 parts of Huoxiang, 7 parts of tartaric acid, 40 parts of a mixture of acetic acid and sodium acetate with a pH value of 6.0, input them into a mixer for stirring, and dry them after stirring evenly, and then input them into a mill for grinding , that is, antiperspirant and antibacterial insole filling powder.
[0034] The content of lead in the bentonite is less than 5 parts per million, the content of cadmium is less than 3 parts per million, the content of arsenic is less than 2 parts per million, the content of mercury is less than 2 parts per million, and the content of copper is less than 2 parts per million 20 / 20.
[0035] The particle fineness after grinding is ≤0.074mm.
[0036] The moisture content after drying is ≤1%.
[0037] The bactericidal effect of the antiperspirant and sterilizing insole filling powder that table 3 embodiment 3 makes
[0038] microorganism
PUM
Property | Measurement | Unit |
---|---|---|
Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap