Method for producing flexographic printing plate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Example
Example 1
Preparation of Photosensitive Resin Composition
[0059]Butadiene latex (Nipol LX111NF containing 55% of non-volatile ingredients; manufactured by Nippon Zeon) (46 parts by mass) and 11 parts by mass of acrylonitrile-butadiene latex (Nipol SX1503 containing 43% of non-volatile ingredients; manufactured by Nippon Zeon); 11 parts by mass of oligobutadiene acrylate (ABU-4S manufactured by Kyoeisha Kagaku), 4.5 parts by mass of lauryl methacrylate (Light Ester L manufactured by Kyoeisha Kagaku) and 4.5 parts by mass of trimethylolpropane triacrylate (Light Ester TMP manufactured by Kyoeisha Kagaku) as photopolymerizable compounds; 0.6 part by mass of a photopolymerization initiator (Irgacure 651); and 12 parts by mass of a hydrophilic polymer (PFT-3 containing 25% of non-volatile ingredients, manufactured by Kyoeisha Kagaku) and 0.06 part by mass of hydroquinone monomethyl ether as other ingredients were mixed in a container to prepare a dope. The dope was poured into a pressurizing
Example
Examples 2 to 14 and Comparative Examples 1 to 5
[0064]The same operation as in Example 1 was conducted except that the composition of the amino-modified silicone in the treatment solution was changed as shown in Table 1 whereby a photosensitive resin composition, a flexographic printing original plate and a flexographic printing plate were prepared.
[0065]The printing plates of Example 1 to 14 and Comparative Examples 1 to 5 were evaluated for uneven application, surface tension, plate surface contamination and uniformity of ink in solid part in accordance with the following evaluating methods.
[0066](1) Evaluation of Uneven Application
[0067]Uneven application was evaluated by checking the uneven application of the solid part by naked eye using the produced printing plate. In case the uneven application was hardly confirmed at a glance, in case it was easily confirmed at a glance and in case viscous uneven application was clearly noted, they were marked as “∘”, “Δ” and “x”, respectively.
PUM
Property | Measurement | Unit |
---|---|---|
Molar mass | aaaaa | aaaaa |
Molar mass | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap