Improve all-steel load-carrying radial tire body rubber material and mixing method thereof
A radial tire and carcass compound technology, applied in the field of improving all-steel radial truck tire carcass compound and its mixing, can solve the problem of low compound hardness and tensile strength, high price of anti-aging agent 4020, and poor adhesion performance and other problems, to achieve the effect of improving the performance of the rubber compound, the processing safety performance, and the tensile stress.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0029] Example 1, an improved all-steel radial truck tire carcass compound, the proportion is by weight, and its components include 100 parts of natural rubber, 46 parts of carbon black N326, 1 part of optimized antioxidant 4020, and antioxidant TMQ 0.9 Parts, 4.5 parts of insoluble sulfur 7020, 1.25 parts of accelerator DZ, 0.2 parts of anti-scorching agent CTP, 5 parts of adhesive RA65, 3 parts of adhesive GLR, 8 parts of active agent, 15 parts of white carbon black.
[0030] The active agent is nano zinc oxide, and the particle size of the nano zinc oxide is 20-80 nm.
[0031] The optimized antioxidant 4020 is an organic complex of N-(1,3 dimethylbutyl)-N'-phenyl-p-phenylenediamine.
[0032] The antioxidant TMQ is 2,2,4-trimethyl-1,2-quinoline dihydroxide polymer.
[0033] The above-mentioned method for mixing the carcass compound includes the following steps:
[0034] 1. One stage mixing: control the temperature of the internal mixing chamber of the internal mixer to 35°C, and the rot
Example Embodiment
[0036] Example 2, an improved all-steel radial truck tire carcass compound, the proportion is by weight, and its components include 100 parts of natural rubber, 46 parts of carbon black N326, 1 part of optimized antioxidant 4020, and antioxidant TMQ 1.05 Parts, insoluble sulfur 7020 4.5 parts, nano zinc oxide 8 parts, accelerator DZ 1.25 parts, anti-scorching agent CTP 0.2 parts, adhesive RA65 5 parts, adhesive GLR20 3 parts, active agent 8 parts, white carbon black 15 Copies.
[0037] The active agent is nano zinc oxide, and the particle size of the nano zinc oxide is 20-80 nm.
[0038] The optimized antioxidant 4020 is an organic complex of N-(1,3 dimethylbutyl)-N'-phenyl-p-phenylenediamine.
[0039] The above-mentioned method for mixing the carcass compound includes the following steps:
[0040] 1. One stage mixing: control the temperature of the internal mixing chamber of the internal mixer to 35°C, and the rotor speed of 80r.min -1 , And then add 100 parts of natural rubber, 1 minu
Example Embodiment
[0043] Example 3, an improved all-steel radial truck tire carcass compound, the proportion by weight, its components include 100 parts of natural rubber, 46 parts of carbon black N326, 1 part of optimized antioxidant 4020, and antioxidant TMQ 1.5 Parts, insoluble sulfur 7020 4.5 parts, nano zinc oxide 8 parts, accelerator DZ 1.25 parts, anti-scorching agent CTP 0.2 parts, adhesive RA65 5 parts, adhesive GLR20 3 parts, active agent 8 parts, white carbon black 15 Copies.
[0044] The active agent is nano zinc oxide, and the particle size of the nano zinc oxide is 20-80 nm.
[0045] The optimized antioxidant 4020 is an organic complex of N-(1,3 dimethylbutyl)-N'-phenyl-p-phenylenediamine.
[0046] The above-mentioned method for mixing the carcass compound includes the following steps:
[0047] 1. One stage mixing: control the temperature of the internal mixing chamber of the internal mixer to 35°C, and the rotor speed of 80r.min -1 , And then add 100 parts of natural rubber, 1 minute later
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap