Preparation method of environment-friendly pervious concrete for highway engineering
A permeable concrete and concrete technology, applied in the field of concrete preparation, can solve the problems of difficult construction control, poor water permeability, poor strength, etc., and achieve the effects of high bearing capacity, high heat dissipation, and long service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0018] Example 1
[0019] An environmentally-friendly water-permeable concrete for highway engineering. The amount of each component of the concrete is 300 parts by weight, 1000 parts of granite gravel, 50 parts of porous silicon carbide ceramic particles, 1 part of polyvinyl acetate, and fiber reinforcement. 50 parts, 30 parts of brightener, 12 parts of coloring agent, 30 parts of water reducing agent and 600 parts of water. Among them, the grain size of granite gravel is 4mm.
[0020] The preparation method of environmentally friendly permeable concrete for highway engineering includes the following steps:
[0021] Firstly, weigh the raw materials according to the mass percentage; secondly, add the emulsion to 10-15 weight multiples of water and stir and mix to obtain an emulsification reagent; then, mix the cement, porous silicon carbide ceramic particles and fiber reinforcement uniformly to form a dry powder , Then add water to the dry powder and stir for 30-60s to obtain a mixtur
Example Embodiment
[0022] Example 2
[0023] An environmentally-friendly water-permeable concrete for highway engineering. According to the parts by weight, the amount of each component of the concrete is: 330 parts of cement, 1200 parts of granite gravel, 60 parts of porous silicon carbide ceramic particles, 2 parts of polyvinyl acetate, and fiber reinforcement 60 parts, 33 parts of brightener, 13 parts of coloring agent, 33 parts of water reducing agent and 700 parts of water. Among them, the grain size of granite gravel is 4mm.
[0024] The preparation method of environmentally friendly permeable concrete for highway engineering includes the following steps:
[0025] Firstly, weigh the raw materials according to the mass percentage; secondly, add the emulsion to 10-15 weight multiples of water and stir and mix to obtain an emulsification reagent; then, mix the cement, porous silicon carbide ceramic particles and fiber reinforcement uniformly to form a dry powder , Then add water to the dry powder and
Example Embodiment
[0026] Example 3
[0027] An environmentally-friendly water-permeable concrete for highway engineering, the concrete is in parts by weight and the amount of each component is: 350 parts of cement, 1300 parts of granite gravel, 70 parts of porous silicon carbide ceramic particles, 1.5 parts of polyvinyl acetate, and fiber reinforcement 65 parts, 35 parts of brightener, 14 parts of coloring agent, 35 parts of water reducing agent and 800 parts of water.
[0028] Among them, the grain size of granite gravel is 4mm.
[0029] The preparation method of environmentally friendly permeable concrete for highway engineering includes the following steps:
[0030] Firstly, weigh the raw materials according to the mass percentage; secondly, add the emulsion to 10-15 weight multiples of water and stir and mix to obtain an emulsification reagent; then, mix the cement, porous silicon carbide ceramic particles and fiber reinforcement uniformly to form a dry powder , Then add water to the dry powder and s
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap