The invention discloses a method for producing a
continuous casting round billet of
wind power tower cylinder
flange steel. The method comprises the steps that the degree of superheat of
continuous casting liquid steel is controlled within the range from 21 DEG C to 25 DEG C in the
continuous casting process;
air water atomizing cooling serves as the cooling mode in a secondary cooling area, the specific
water flow is controlled within the range from 0.15 L / kg to 0.18 L / kg, the
casting speed is controlled within the range from 0.30 m / min to 0.34 m / min, the current of
electromagnetic stirring of a crystallizer is controlled within the range from 200 A to 300 A, the frequency of
electromagnetic stirring of the crystallizer is controlled within the range from 2.0 Hz to 3.0 Hz, the current of
electromagnetic stirring of the
tail end of solidification is controlled within the range from 350 A to 400 A, and the frequency electromagnetic stirring of the
tail end of solidification is controlled within the range from 8 Hz to 12 Hz. According to the method, the surface quality and interior quality of the continuous
casting round billet of
wind power tower cylinder
flange steel can be effectively improved by setting and optimizing technological parameters. In addition, a finished
wind power tower cylinder
flange machined through the round billet obtained according to the method can completely meet the quality requirement of the wind
power tower cylinder flange steel after ultrasonic flaw detection.