Anti-radiation post-treatment method of latex gloves
A latex glove, anti-radiation technology, applied in the field of anti-radiation post-treatment of latex gloves, can solve the problems of poor air permeability of gloves, uncomfortable wearing, poor durability of anti-radiation, etc. Effects of Radiation Ability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0022] A radiation-resistant aftertreatment method for latex gloves, comprising the steps of:
[0023] (1) After the latex base material is added to the glove model, the microwave radiation modification finishing process is carried out: the glove model with the latex base material is placed in a microwave radiation device, and after microwave radiation at a power of 450W for 20s; spray on the surface of the glove model A layer of nano-titanium dioxide solution with a mass fraction of 3%; adjust the power to 350W and continue microwave irradiation for 0.5min, take it out, wash it with water for 3 times, and microwave it until it is 90% dry to continue latex vulcanization, dipping, leaching, film drying, and demoulding Process to obtain semi-finished latex gloves;
[0024] (2) Anti-radiation finishing agent treatment process: place the latex glove semi-finished product in an anti-radiation finishing agent containing 70% anti-radiation plant extract, 3% citric acid solution, and the
Embodiment 2
[0028] A radiation-resistant aftertreatment method for latex gloves, comprising the steps of:
[0029] (1) After the latex base material is added to the glove model, the microwave radiation modification finishing process is carried out: the glove model with the latex base material is placed in a microwave radiation device, and after microwave radiation at a power of 550W for 20s; spray on the surface of the glove model A layer of nano-titanium dioxide solution with a mass fraction of 3%; adjust the power to 350W and continue microwave irradiation for 2 minutes, take it out, wash it with water for 3 times, and microwave it until it is 90% dry to continue the process of latex vulcanization, dipping, leaching, film drying, and demoulding Get semi-finished latex gloves;
[0030] (2) Anti-radiation finishing agent treatment process: place the latex glove semi-finished product in an anti-radiation finishing agent containing 70% anti-radiation plant extract, 3% citric acid solution, and
Embodiment 3
[0034] A radiation-resistant aftertreatment method for latex gloves, comprising the steps of:
[0035] (1) After the latex base material is added to the glove model, the microwave radiation modification finishing process is carried out: the glove model with the latex base material is placed in a microwave radiation device, and after microwave radiation at a power of 510W for 16s; spray on the surface of the glove model A layer of nano-titanium dioxide solution with a mass fraction of 3%; adjust the power to 350W and continue microwave irradiation for 0.8min, take it out, wash it twice with water, and microwave it to 90% dry to continue latex vulcanization, dipping, leaching, film drying, and demoulding Process to obtain semi-finished latex gloves;
[0036] (2) Anti-radiation finishing agent treatment process: place the latex glove semi-finished product in an anti-radiation finishing agent containing 70% anti-radiation plant extract, 3% citric acid solution, and the rest of deioni
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap