Wear-resistant sealing gasket and preparation method thereof
A gasket and modification technology, applied in the field of wear-resistant gaskets and their preparation, can solve the problems that the gasket affects the running time of equipment and the sealing performance of the gasket equipment, etc., so as to shorten the preparation time, improve the running time and wear resistance. good effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0032] The present invention also includes the preparation method of the above-mentioned wear-resistant gasket, comprising the steps of:
[0033] S1 Put vinyl polydimethylsiloxane, nano silicon dioxide, mercaptan-modified neoprene rubber, acrylonitrile butadiene rubber, and hexamethyldisiloxane into the defoaming mixer in turn, and stir for 5- 20 minutes;
[0034] S2 Pour the stirred raw materials into the mold of the vulcanizer, heat and press to obtain a semi-finished product;
[0035] S3 processes semi-finished products into wear-resistant gaskets.
[0036] The temperature of heating and pressing in the step S2 is 160-180 degrees, and the pressing is 0.5-0.8Mpa.
[0037] The duration of step S2 is 10-30 minutes.
[0038] Step S1 puts the raw materials into the defoaming mixer in multiple batches.
Embodiment 1
[0040] A wear-resistant sealing gasket, comprising in parts by mass: 100 parts of vinyl polydimethylsiloxane, 12 parts of nano-silica, 40 parts of mercaptan-modified neoprene rubber, and 6 parts of acrylonitrile butadiene rubber , 56 parts of hexamethyldisiloxane; the nano-silica selects the nano-silica whose specific surface area is 460m2 / g. Mercaptan-modified chloroprene rubber is obtained by polymerization of chloroprene in an octyl mercaptan environment.
[0041] The content of acrylonitrile in the acrylonitrile butadiene rubber is 36%.
[0042] A preparation method for a wear-resistant sealing gasket, comprising the steps of:
[0043] S1 Put vinyl polydimethylsiloxane, nano-silica, mercaptan-modified neoprene rubber, acrylonitrile butadiene rubber, and hexamethyldisiloxane into a defoaming mixer in turn, and stir for 5 minutes ;
[0044] S2 Pour the stirred raw materials into the mold of the vulcanizer, heat and press to obtain a semi-finished product;
[0045] S3 proc
Embodiment 2
[0049] A wear-resistant sealing pad, comprising in parts by mass: 120 parts of vinyl polydimethylsiloxane, 10 parts of nano silicon dioxide, 40 parts of mercaptan-modified neoprene rubber, and 10 parts of acrylonitrile butadiene rubber , 60 parts of hexamethyldisiloxane;
[0050] The content of acrylonitrile in the acrylonitrile butadiene rubber is 40%.
[0051] The preparation method of above-mentioned wear-resisting gasket, comprises the steps:
[0052] S1 Put vinyl polydimethylsiloxane, nano silicon dioxide, mercaptan-modified chloroprene rubber, acrylonitrile butadiene rubber, and hexamethyldisiloxane into the defoaming mixer three times, and stir for 15 minute;
[0053] S2 Pour the stirred raw materials into the mold of the vulcanizer, heat and press to obtain a semi-finished product;
[0054] S3 processes semi-finished products into wear-resistant gaskets.
[0055] The temperature of heating and pressing in the step S2 is 180 degrees, and the pressing is 0.7Mpa. The du
PUM
Property | Measurement | Unit |
---|---|---|
Specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap