Box sealing mud strip for casting and preparation method thereof
A mud strip and strip technology, which is applied to the field of sealing mud strips for casting and its preparation, can solve the problems of poor plasticity, short storage period, low refractoriness, etc., and achieves reduction of water loss, reduction of sealing errors, and improvement of fire resistance. sexual effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0025] Example 1
[0026] A reservoir clavicle is made of casting, wherein the following components are composed of weight percent:
[0027] Environmentally friendly plasticizer 40%
[0028] Furnishing mud 55%
[0029] 5% of fibrous filler
[0030] After the above components are mixed and extruded to form a strip, there is a layer of refractory anti-stick materials thereof.
[0031] Among them, environmentally friendly plasticizers are epoxy soybean oil.
[0032] The water resistance rate of the refractory is 2%.
[0033] The fibrous filler is one or a combination of cotton or textile fragments.
[0034] Refractory anti-stick materials are ceramic fiber fragments having a particle diameter of less than 1 mm.
[0035] The preparation method of the above-described casting sealing clay includes the following specific steps:
[0036] a) Taking a mass fraction, 40% of the environmentally friendly plasticizer, 55% of the refractory mud material, 5% fibrous filler is mixed to obtain a premi
Example Embodiment
[0038] Example 2
[0039] A reservoir clavicle is made of casting, wherein the following components are composed of weight percent:
[0040] Environmentally friendly plasticizer 45%
[0041] 47% of fire resistant mud
[0042] Fibrillary filler 8%
[0043] After the above components are mixed and extruded to form a strip, there is a layer of refractory anti-stick materials thereof.
[0044] Among them, environmentally friendly plasticizers are epoxy soybean oil.
[0045] The water resistance rate of the refractory is 1.5%.
[0046] The fibrous filler is one or a combination of cotton or textile fragments.
[0047] Refractory anti-stick materials are ceramic fiber fragments having a particle diameter of less than 1 mm.
[0048] The preparation method of the above-described casting sealing clay includes the following specific steps:
[0049] a) Take 45% of the environmentally friendly plasticizer, 47% of the fireproofer, 8% of the fibrous filler to obtain a premix by mass fraction.
[0
Example Embodiment
[0051] Example 3
[0052] A reservoir clavicle is made of casting, wherein the following components are composed of weight percent:
[0053] Environmentally friendly plasticizer 48%
[0054] 50% of fire resistant mud
[0055] 3% of fibrous filler
[0056] After the above components are mixed and extruded to form a strip, there is a layer of refractory anti-stick materials thereof.
[0057] Among them, environmentally friendly plasticizers are epoxy soybean oil.
[0058] The water resistance rate of the refractory is 1.5%.
[0059] The fibrous filler is one or a combination of cotton or textile fragments.
[0060] Refractory anti-stick materials are ceramic fiber fragments having a particle diameter of less than 1 mm.
[0061] The preparation method of the above-described casting sealing clay includes the following specific steps:
[0062] a) A premix is mixed by 48% environmentally friendly plasticizer, 50% of the fibrous filler by mass fraction, and 3% of the fibrous filler to obt
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap