Aqueous porcelain imitating coating material

A kind of imitation porcelain coating, water-based technology, applied in the direction of coating, can solve the problem of insufficient water resistance, and achieve good overall effect.

Inactive Publication Date: 2013-01-02
NANTONG XINGYU PAINT
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

This new type of paints that are very durable when painted on ceramics can be made without any cracks or other imperfections during production process. It also works well with different types of surfaces such as glasses, plates, stoves, etc., making them ideal for use over various industries including construction industry.

Problems solved by technology

This patented technical problem addressed by this patents relates to improving the quality of painted ceramics without compromising their durability or ease of use for creating various types of objects such as furniture that require high levels of strength against damage caused during cleanings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] The water-based enamel-like coating of the present embodiment comprises the following components: 25 parts by weight of water-soluble polyvinyl alcohol emulsion, 20 parts by weight of titanium dioxide, 20 parts by weight of calcium carbonate, 0.6 parts by weight of methyl cellulose, and 0.4 parts by weight of ethyl cellulose , 70 parts by weight of distilled water.

Embodiment 2

[0011] The water-based enamel-like coating of the present embodiment comprises the following components: 30 parts by weight of water-soluble polyvinyl alcohol emulsion, 15 parts by weight of titanium dioxide, 25 parts by weight of calcium carbonate, 0.5 parts by weight of methyl cellulose, and 0.5 parts by weight of ethyl cellulose , 75 parts by weight of distilled water.

Embodiment 3

[0013] The water-based enamel-like coating of the present embodiment comprises the following components: 20 parts by weight of water-soluble polyvinyl alcohol emulsion, 25 parts by weight of titanium dioxide, 15 parts by weight of calcium carbonate, 0.7 parts by weight of methyl cellulose, and 0.3 parts by weight of ethyl cellulose , 65 parts by weight of distilled water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention provides an aqueous porcelain imitating coating material, which comprises the following components, by weight, 20-30 parts of a water-soluble polyvinyl alcohol emulsion, 15-25 parts of titanium dioxide powder, 15-25 parts of calcium carbonate, 0.5-0.7 part of methyl cellulose, 0.3-0.5 part of ethyl cellulose, and 65-75 parts of distilled water. The aqueous porcelain imitating coating material of the present invention has the following technical effects that: the coating material belongs to a high gloss coating material, no brick seam exists after dyeing with the coating material, the whole effect is good, and the coating material has the same characteristics as the characteristics of water resistance, alkali resistance, scrub resistance, and the like of the porcelain tile.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner NANTONG XINGYU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap