Low-temperature early-strength toughening cement slurry and method for preparing same

A low-temperature early strength agent and cement slurry technology, applied in the field of cement slurry, can solve problems such as no successful experience, and achieve the effects of good stability, increased compressive strength and toughness, and low water loss

Active Publication Date: 2016-05-11
RES INST OF SHAANXI YANCHANG PETROLEUM GRP
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the research on low-temperature cement slurry system is only applied to offshore surface cementing and onshore shallow high-permeability wells that do not need fracturing. When the strength development is required, it still needs to have a certain toughness. During

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature early-strength toughening cement slurry and method for preparing same
  • Low-temperature early-strength toughening cement slurry and method for preparing same
  • Low-temperature early-strength toughening cement slurry and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Weigh 100 parts by weight of high-resistance oil well cement, 1.8 parts by weight of low-temperature early-strength agent, 1.8 parts by weight of cementing agent, 0.8 parts by weight of drag reducer, and 2 parts by weight of low-temperature toughening agent, and dry mix it into a solid mixture; Take 44 parts by weight of water, 0.8 parts by weight of fluid loss reducer, and 0.2 parts by weight of defoamer and mix them into a solution in the stirring blade cup; pour the solid mixture into the stirring blade within 15 seconds at the speed of 4000±200r / min In the cup, stir at 12000 ± 500r / min at a high speed for 35s to prepare the low-temperature early-strength toughening cement slurry of the present invention. get as figure 1 The thickening curve shown.

Embodiment 2

[0033] Weigh 100 parts by weight of high-resistance oil well cement, 1.5 parts by weight of low-temperature early strength agent, 1.8 parts by weight of cementing agent, 0.8 parts by weight of drag reducer, and 2 parts by weight of low-temperature toughening agent, and dry mix it into a solid mixture; Take 44 parts by weight of water, 0.8 parts by weight of fluid loss reducer, and 0.2 parts by weight of defoamer and mix them into a solution in the stirring blade cup; pour the solid mixture into the stirring blade within 15 seconds at the speed of 4000±200r / min In the cup, stir at a speed of 12000±500r / min for 35s to prepare low-temperature early-strength toughening cement slurry. figure 2 The thickening curve shown.

Embodiment 3

[0035] Weigh 100 parts by weight of high-resistance oil well cement, 1.0 parts by weight of low-temperature early-strength agent, 1.8 parts by weight of cementing agent, 0.8 parts by weight of drag reducer, and 2 parts by weight of low-temperature toughening agent, and dry mix it into a solid mixture; Take 44 parts by weight of water, 0.8 parts by weight of fluid loss reducer, and 0.2 parts by weight of defoamer and mix them into a solution in the stirring blade cup; pour the solid mixture into the stirring blade within 15 seconds at the speed of 4000±200r / min In the cup, stir at a speed of 12000±500r / min for 35s at high speed to prepare low-temperature early-strength toughening cement slurry. image 3 The thickening curve shown.

[0036] The low-temperature early-strength cement slurry system of the present invention has good stability, low water loss, and can significantly increase the compressive strength and toughness of cement stones at low temperatures, such as Figure

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses low-temperature early-strength toughening cement slurry and a method for preparing the same, relates to cement slurry used during well cementing and belongs to the technical field of oil and gas well cementing engineering. By the aid of the low-temperature early-strength toughening cement slurry and the method, inherent shortcomings of slow strength development and high brittleness of cement stone at low temperatures can be solved. The low-temperature early-strength toughening cement slurry comprises, by weight, 100 parts of oil well cement, 1-2 parts of low-temperature early-strength agents, 1-2 parts of cementing agents, 1-4 parts of low-temperature toughening agents, 0.8-1.2 parts of PVA (polyvinyl acetate) fluid loss agents, 0.8 part of acetone formaldehyde condensation compound drag reducing agents, 0.2 part of defoamers and the balance clear water. A mass ratio of the clear water to the oil well cement is 0.44:1, and the density of the cement slurry is 1.85g/cm<3>-1.90g/cm<3>. The low-temperature early-strength toughening cement slurry and the method have the advantages that the low-temperature early-strength toughening cement slurry is excellent in stability and low in fluid loss characteristics, and the compressive strength and the toughness of cement stone at low temperatures can be obviously improved.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner RES INST OF SHAANXI YANCHANG PETROLEUM GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap