Mobile phone shell and injection molding technology thereof
A technology of mobile phone shell and process, applied in the direction of coating, etc., can solve the problems of high processing cost and lack of core cost market competitiveness, and achieve the effect of simple method, shortening processing time and reducing cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] Embodiment 1 proposes a kind of injection molding process of mobile phone case, comprises the following steps:
[0017] (1) Firstly, the aluminum sheet is dried at 115°C for 26 hours until its moisture content is not higher than 0.02%.
[0018] (2) Carry out CNC processing and injection molding of the product obtained in the step (1) at a temperature of 275° C., and sequentially prepare the mobile phone case shell and the antenna slot, positioning hole, art slot, and inner cavity on the mobile phone case shell , earphone hole, USB hole, camera and flash hole. Wherein, the injection molding pressure is 90MPa-110MPa, and the mold temperature is 110°C.
[0019] (3) An annealing method is used for heat treatment to obtain a mobile phone case; wherein, the annealing rate is 3°C / min, and the heat treatment temperature is 125°C.
Embodiment 2
[0021] Embodiment 2 proposes a kind of injection molding process of mobile phone case, comprises the following steps:
[0022] (1) Firstly, the aluminum sheet is dried at 125°C for 22 hours until its moisture content is not higher than 0.02%.
[0023] (2) Carry out CNC processing and injection molding of the product obtained in the step (1) at a temperature of 300° C., and sequentially prepare the mobile phone case shell and the antenna slot, positioning hole, art slot, and inner cavity on the mobile phone case shell , earphone hole, USB hole, camera and flash hole. Wherein, the injection molding pressure is 90MPa, and the mold temperature is 110°C.
[0024] (3) An annealing method is used for heat treatment to obtain a mobile phone case; wherein, the annealing rate is 3°C / min, and the heat treatment temperature is 125°C.
Embodiment 3
[0026] Embodiment 3 proposes a kind of injection molding process of mobile phone case, comprises the following steps:
[0027] (1) Firstly, the aluminum sheet is dried at 120°C for 24 hours until the moisture content is not higher than 0.02%.
[0028] (2) Carry out CNC processing and injection molding of the product obtained in the step (1) at a temperature of 2850° C., and sequentially prepare the mobile phone case shell and the antenna slot, positioning hole, art slot, and inner cavity on the mobile phone case shell , earphone hole, USB hole, camera and flash hole. Wherein, the injection molding pressure is 90MPa-110MPa, and the mold temperature is 100°C.
[0029] (3) An annealing method is used for heat treatment to obtain a mobile phone case; wherein, the annealing rate is 5°C / min, and the heat treatment temperature is 105°C.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap