Mineral ceramic and preparation method thereof
A technology of minerals and ceramics, applied in the field of ceramic materials, can solve the problems of high content, harmful to people, insufficient energy conservation and environmental protection, etc., and achieves the effect of simple preparation process, beneficial to production and manufacturing, and good market promotion value.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] A kind of mineral ceramics, the mineral ceramics comprises the following raw materials according to mass percentage: potassium feldspar 6%, silicon dioxide 10%, diopside 4%, spodumene 3%, medical stone 8%, sodium 2% feldspar, 2% quartz, 2% bentonite, 3% clay, 20% volcanic rock, and the rest is kaolin.
[0017] A preparation method of mineral ceramics, comprising the following steps:
[0018] (1) Calcinate potassium feldspar, spodumene, volcanic rock, diopside and medical stone at 800°C for 3 hours, cool to room temperature, grind them, pass through a 200-mesh sieve, and set aside; Stone and quartz were calcined at 900°C for 2 hours, cooled to room temperature, ground, passed through a 40-mesh sieve, and set aside; kaolin, clay, and bentonite were calcined at 700°C for 2 hours, cooled to room temperature, ground, passed through a 150-mesh sieve, set aside ;
[0019] (2) Put the above raw materials into a ball mill together, add water of 0.7 times the total weight of the r
Embodiment 2
[0022] A kind of mineral ceramics, the mineral ceramics comprises the following raw materials according to mass percentage: 12% potassium feldspar, 16% silicon dioxide, 7% diopside, 6% spodumene, 10% medical stone, sodium 4% feldspar, 5% quartz, 6% bentonite, 7% clay, 26% volcanic rock, and the rest is kaolin.
[0023] A preparation method of mineral ceramics, comprising the following steps:
[0024] (1) Calcinate potassium feldspar, spodumene, volcanic rock, diopside and medical stone at 820°C for 4 hours, cool to room temperature, grind them, pass through a 300-mesh sieve, and set aside; Stone and quartz were calcined at 920°C for 4 hours, cooled to room temperature, ground, passed through a 80-mesh sieve, and set aside; kaolin, clay, and bentonite were calcined at 800°C for 4 hours, cooled to room temperature, ground, passed through a 200-mesh sieve, set aside ;
[0025] (2) Put the above raw materials into a ball mill together, add water of 0.7 times the total weight of the
Embodiment 3
[0028] A kind of mineral ceramics, said mineral ceramics comprises the following raw materials according to mass percentage: potassium feldspar 11%, silicon dioxide 15%, diopside 6%, spodumene 5%, medical stone 9%, sodium Feldspar 3%, Quartz 4%, Bentonite 5%, Kaolin 12%, Volcanic Rock 25%, Clay 5%.
[0029] A preparation method of mineral ceramics, comprising the following steps:
[0030] (1) Calcinate potassium feldspar, spodumene, volcanic rock, diopside and medical stone at 810°C for 3.5 hours, cool to room temperature, grind them, pass through a 250-mesh sieve, and set aside; Feldspar and quartz were calcined at 910°C for 3 hours, cooled to room temperature, ground, passed through a 60-mesh sieve, and set aside; kaolin, clay and bentonite were calcined at 750°C for 3 hours, cooled to room temperature, ground, passed through a 180-mesh sieve, spare;
[0031] (2) Put the above raw materials into a ball mill together, add water 0.6 times of the total weight of the raw material
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap