Aluminium bus vertical casting technology method
A casting process and aluminum bus bar technology, which is applied in the field of aluminum bus bar vertical casting process, can solve the problems of high production cost, complex process manufacturing, uneven current, etc., and achieve the effect of improving product qualification rate and reducing manufacturing cost
Inactive Publication Date: 2008-02-20
GUIZHOU BRANCH CHINA ALUMINUM IND
View PDF0 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
In the past, rolling and calendering busbars were used in electrolytic cell aluminum busbars, which had a series of disadvantages: complex manufacturing process, high energy consumption, serious anisotropy, uneven current, high connection voltage and high production costs, etc.
But its production technology is difficult to master, and the product quality is unstable
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0012] Example
[0013] Please write the specific name of the casting equipment, control it during casting, and control the pressure of the cooling water at 0.8~1.0kg / cm 2 (Pump head H=32m, flow Q=100m 3 / h).
[0014] Table 1 List of Fe / Si, process parameters and product qualification rate of cast aluminum bus
[0015]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The present invention relates to a technical method for vertical casting of aluminum bus. By adopting the technique of vertical casting the invention is characterzied in that the technological parameters in production are as follows: 1) aluminum content in aluminum liquid used in casting is more than 99.65 percent, content of impurity is less than 0.35 percent, and ratio of Fe to Si is limited between 1.2 to 1.5; 2) casting termperature is limited between 720 to 730 DEG C; 3) casting speed is controlled between 80 to 100mm per minute; 4) the distant between level of the aluminum liquid and the upper inner rim of crystallizer is 2.0cm. The present method can remarkably improve the passing rate of product. In practical production, the present method can control heat crack, curve and twist of the aluminum bus and can reduce the production cost of the aluminum bus.
Description
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Owner GUIZHOU BRANCH CHINA ALUMINUM IND
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap