Multifunctional wood protection agent based on nano silica sol and preparation method of multifunctional wood protection agent
A nano-silica sol, multi-functional technology, applied in wood treatment, wood impregnation, wood impregnation, etc., to achieve the effects of improved control efficiency, reduced water absorption, and improved dimensional stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] (1) get concentration 20%, alkaline silica sol 352g, potassium carbonate 14g, borax 12g, manganese chloride 20g, phosphoric acid 6g of particle diameter<20nm;
[0029] (2) add salt of wormwood to silica sol, keep stirring during adding, until salt of salt dissolves completely, then add borax, after adding borax, add phosphoric acid while stirring, until borax dissolves completely;
[0030] (3) After the borax is completely dissolved, add manganese chloride, which is now called current use and kept dry before use;
[0031] (4) Stir the finally obtained mixed solution for 30 min to obtain.
Embodiment 2
[0033] (1) get concentration 10%, alkaline silica sol 340g, potassium carbonate 20g, borax 16g, manganese chloride 28g, phosphoric acid 12g of particle diameter<20nm;
[0034] (2) add salt of wormwood to silica sol, keep stirring during adding, until salt of salt dissolves completely, then add borax, after adding borax, add phosphoric acid while stirring, until borax dissolves completely;
[0035] (3) After the borax is completely dissolved, add manganese chloride, which is now called current use and kept dry before use;
[0036] (4) Stir the finally obtained mixed solution for 60 min to obtain.
Embodiment 3
[0038] (1) get concentration 30%, alkaline silica sol 368g, potassium carbonate 8g, borax 8g, manganese chloride 12g, phosphoric acid 2g of particle diameter<20nm;
[0039] (2) add salt of wormwood to silica sol, keep stirring during adding, until salt of salt dissolves completely, then add borax, after adding borax, add phosphoric acid while stirring, until borax dissolves completely;
[0040] (3) After the borax is completely dissolved, add manganese chloride, which is now called current use and kept dry before use;
[0041] (4) Stir the finally obtained mixed solution for 15 minutes to obtain.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap