A preparation process and fluororubber technology, which is applied in the field of high-temperature bonding and shaping preparation technology, can solve the problems of oven pipeline fire, explosion injury, fire, etc., and achieve the effects of reliable use, non-foaming adhesion, and good softness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] The invention provides a technical solution:
[0020] A high-temperature bonding and shaping preparation process based on mesh aramid fluororubber cloth, including aramid mesh cloth and fluororubber. The rubber and the aramid mesh are placed together in a vulcanizing machine for vulcanization.
[0021] Include the following steps:
[0022] Step 1: Take the aramid mesh cloth, use a layer of aramid mesh cloth as the base cloth, flatten the aramid mesh cloth, cut it to a suitable size, and collect the sorted aramid mesh cloth;
[0023] Step 2: Carry out metal detection inspection on the fluororubber, take out the detected metal particles, put the inspected fluororubber into the open mill for processing, and return the fluororubber to the natural temperature;
[0024] Step 3: Adjust the roll distance of the calendering rollers in the three-roll calender, and use the three-roll calender to calender the fluororubber to the required thickness and width of the fluororubber rubbe
Embodiment 2
[0030] The invention provides a technical solution:
[0031] A high-temperature bonding and shaping preparation process based on mesh aramid fluororubber cloth, including aramid mesh cloth and fluororubber. The rubber and the aramid mesh are placed together in a vulcanizing machine for vulcanization.
[0032] Include the following steps:
[0033] Step 1: Take the aramid mesh cloth, use a layer of aramid mesh cloth as the base cloth, flatten the aramid mesh cloth, cut it to a suitable size, and collect the sorted aramid mesh cloth;
[0034] Step 2: Carry out metal detection inspection on the fluororubber, take out the detected metal particles, put the inspected fluororubber into the open mill for processing, and return the fluororubber to the natural temperature;
[0035] Step 3: Adjust the roll distance of the calendering rollers in the three-roll calender, and use the three-roll calender to calender the fluororubber to the required thickness and width of the fluororubber rubbe
Embodiment 3
[0041] The invention provides a technical solution:
[0042] A high-temperature bonding and shaping preparation process based on mesh aramid fluororubber cloth, including aramid mesh cloth and fluororubber. The rubber and the aramid mesh are placed together in a vulcanizing machine for vulcanization.
[0043] Include the following steps:
[0044] Step 1: Take the aramid mesh cloth, use a layer of aramid mesh cloth as the base cloth, flatten the aramid mesh cloth, cut it to a suitable size, and collect the sorted aramid mesh cloth;
[0045] Step 2: Carry out metal detection inspection on the fluororubber, take out the detected metal particles, put the inspected fluororubber into the open mill for processing, and return the fluororubber to the natural temperature;
[0046] Step 3: Adjust the roll distance of the calendering rollers in the three-roll calender, and use the three-roll calender to calender the fluororubber to the required thickness and width of the fluororubber rubbe
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction