Method for preparing villiaumite and lithium salt by using high-lithium electrolyte
A technology of electrolyte and lithium salt, which is applied in the field of aluminum electrolyte recycling, can solve the problems of low molecular ratio of recycled cryolite, low electrolyte molecule, shrinking cryolite market demand, etc., and achieve the effect of high recovery rate and large market demand
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0041] Example 1
[0042] This embodiment provides a method of preparing fluorine salts and lithium salts using high lithium electrolytes, including:
[0043] A 100 kg of particles and 80 kg of aluminum sulfate were added to 300 mesh, and then mixed with a 150 kg of mass fraction of 5% sulfuric acid to be uniformly mixed, and the electrolyte particles were prepared. NA 3 Alf 6 76%, NA 5 Al 3 Fly 14 The content is 8%, the LIF content is 8%, C content 2%, CAF 2 3.2%, Al 2 O 3 The content is 2.8%; the mixed slurry of the feedstock is not smashed to a particle size of less than 120 μm, and inserted into the rotary furnace, calcined by 2 h at 500 ° C, and then add 320 kg of pure water, wet to less than 200 mesh, filtered after filter residue 0.0 ° C dry, resulting in a 75 kg fluorine salt mixture; an XRD semi-quantitative analysis method was used to detect the ingredients of the fluorine salt mixture. figure 2 As shown, the main component of the fluorine salt mixture is NA 3 Alf 6 NA 5 Al
Example Embodiment
[0046] Example 2
[0047] This embodiment provides a method of preparing fluorine and lithium salts using a high lithium electrolyte, comprising: first picking 1000 kg of particles of less than 25 mm, 1000 kg of octave, aluminum sulfate, and aluminum, mixed, mixed to 400 mesh, The raw material mixed slurry is made uniformly mixed with 1200 kg of mass fraction of 30% of sulfuric acid, wherein the electrolyte particles comprise Na. 3 Alf 6 Included 80%, NA 5 Al 3 Fly 14 The content is 6%, the LIF content is 4%, C content 2.5%, CAF 2 Content 2.5%, Al 2 O 3 The content is 5%; the mixed slurry of the feedstock is not less than 150 μm, and the rotary furnace is injected into the rotary furnace, and the calcination of 600 ° C is calcined. After cooling, the pure water is added to less than 200 mesh, and the filtered filter is dried at 500 ° C. The 780 kg fluorine salt mixture was obtained, and the ingredients of the fluorine salt mixture were detected by XRD semi-quantitative analysis metho
Example Embodiment
[0050] Example 3
[0051] This embodiment provides a method of preparing fluorine and lithium salts using a high lithium electrolyte, including electrolyte particles having a 500 kg of particle size of less than 25 mm, 350 kg sulfate and 350 kg of aluminum sulfate, mixed grinding to 400 mesh Further, it is uniformly mixed with a 50% sulfuric acid solution having a 250 kg mass fraction of 50%, wherein the electrolyte particles comprise Na. 3 Alf 6 74% content, NA 5 Al 3 Fly 14 The content is 7%, the LIF content is 10%, C content 2.5%, CAF 2 3.2%, Al 2 O 3 The content is 3.3%; the mixed slurry of the raw material is not less than 150 μm, and the rotary furnace is injected into the rotary furnace, and 1 H is calcined at 550 ° C. After cooling, add 1500 kg of pure water, wet grinding to less than 200 mesh, filtered after filter residue It was dried at 550 ° C to give 315 kg of fluorine salt mixture, and the ingredients of the fluorine salt mixture were detected by XRD semi-quantitative a
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap