Diaphragm with excellent cohesiveness and air permeability and preparation method thereof
A gas-permeable and cohesive technology, applied in the direction of separators/films/diaphragms/spacers, electrical components, structural parts, etc., can solve the problems of poor comprehensive performance of the diaphragm, achieve a small cross-overlapping range, and ensure stability performance, to ensure the effect of breathability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0039] The present application also provides a method for preparing a separator with excellent adhesion and air permeability, comprising the following steps:
[0040]S1. Prepare PVDF primary particles 211 by emulsion polymerization, the particle size D50 of the primary particles 211 is 50 nm-500 nm, and the primary particles 211 are polymerized into secondary particles 212, and the particle size D50 of the secondary particles 212 is 0.5 μm-20 μm; S2. Mix the secondary particles 212, PMMA microspheres, binder, and deionized water according to a preset weight ratio. The particle size of the added PMMA microspheres is 1-15 μm, and the PMMA content accounts for 5-30% of PVDF. The solid content of the bonding slurry is 10-30%, the binder accounts for 1-20% of the secondary particles 212, and a uniform bonding slurry is formed by stirring; S3. Use a rotary nozzle to spray the bonding slurry on one side of the base film Step 10, the spray flow rate of the rotary nozzle is 50-500ml / min
Example Embodiment
[0048] Example 1:
[0049] S1. Preparation of secondary particles 212
[0050] The PVDF primary particles 211 were prepared by emulsion polymerization with D50 of 240 nm, washed, spray-dried and sieved to obtain PVDF secondary particles 212, wherein the PVDF powder particle size D50 was 6.2 μm.
[0051] S2, configure the adhesive paste
[0052] A binder solution with a mass fraction of 15%, the binder is styrene-butadiene latex, PVDF, binder, and deionized water are mixed, and a uniform slurry is formed by stirring. The speed of the mixer is 700rpm, and the solid content of the slurry is 20%. , in which the binder accounts for 7.5% of the mass of PVDF.
[0053] S3, spraying
[0054] The slurry is uniformly sprayed on the surface of the 9-micron PE base film 10 on one side, the flow rate of a single rotary spraying equipment is 150 ml / min, and the speed is 10000rpm;
[0055] S4, drying to obtain diaphragm B1
[0056] The coated separator was placed in an oven and fully drie
Example Embodiment
[0057] Example 2:
[0058] The difference from Example 1 is that the secondary particles 212 of PVDF are not stacked, and the primary particles 211 are directly used for the subsequent preparation of the spraying slurry. The other steps remain unchanged, and the diaphragm B2 is obtained. 0.64g / m 2 .
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap