Preparation method for triphase mixed crystal titanium dioxide materials
A titanium dioxide and mixed technology, applied in the field of photocatalysis, can solve the problems of unfavorable popularization and application, complicated operation, high energy consumption, etc., and achieve good photocatalytic purification effect, small material particle size and high crystallinity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0018] Example 1:
[0019] Add 4.4 mL of butyl titanate to 50 mL of 10 mol / L sodium hydroxide solution and continue stirring for 5 hours; wash the resulting precipitate with 150 mL of water 3 times, redisperse it in 40 mL of 0.25 mol / L nitric acid solution, and stir 30 min; Place the resulting mixture in a 100 mL hydrothermal reaction kettle with a tetrafluoroethylene liner, and hydrothermally react at 180°C for 24 h; wash the resulting precipitate with water until the supernatant is neutral, and dry it at 50°C. For details, please refer to figure 1 , figure 1 This is the X-ray diffraction (XRD) pattern of the three-phase mixed crystal titanium dioxide prepared in this example.
Example Embodiment
[0020] Example 2:
[0021] Add 4.4 mL of isopropyl titanate to 50 mL of 10 mol / L sodium hydroxide solution and continue to stir for 5 h; wash the resulting precipitate with 150 mL of water three times and redisperse it in 40 mL of 0.25 mol / L hydrochloric acid solution. Stir for 30 min; place the resulting mixture in a 100 mL hydrothermal reaction kettle with a tetrafluoroethylene liner, and react hydrothermally at 180°C for 24 h; wash the resulting precipitate with water until the supernatant is neutral, and dry it at 50°C to obtain .
Example Embodiment
[0022] Example 3:
[0023] Add 4.4 mL of butyl titanate to 100 mL of 8 mol / L potassium hydroxide solution and keep stirring for 5 h; wash the resulting precipitate with 150 mL of water 3 times, redisperse it in 40 mL of 0.25 mol / L hydrochloric acid solution, and stir 30 min; Place the resulting mixture in a 100 mL hydrothermal reaction kettle with a tetrafluoroethylene liner, and hydrothermally react at 180°C for 24 h; wash the resulting precipitate with water until the supernatant is neutral, and dry it at 50°C.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap