Phenolic resin molding material
A technology of phenolic resin and molding materials, applied in the field of phenolic resin molding materials, which can solve the problems of quality stability decline and achieve the effects of taking into account the molding cycle, shortening the moldability, and excellent thermal stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0046] Example
[0047] Hereinafter, the phenol resin molding material of the present invention will be explained by examples and comparative examples, but the present invention is not limited by these examples at all.
[0048] The material mixture blended in the proportions (parts by mass) shown in Table 1 was kneaded by heating rollers with different rotation speeds, and cooled into flakes, and the cooled material was pulverized to obtain granular molding materials. Table 1 shows the workability at the time of manufacturing the molding material and the performance evaluation results of the molded product obtained by molding the molding material. In addition, the kneading conditions of the heating roll are set at high speed side / low speed side=20 / 14rpm, temperature at high speed side / low speed side=90 / 20℃, and set the fluidity between 5-10 Adjust the mixing time between minutes.
[0049] The complexes used in the examples and comparative examples are as follows
[0050] (1) Ph
PUM
Property | Measurement | Unit |
---|---|---|
Acid value | aaaaa | aaaaa |
Acid value | aaaaa | aaaaa |
Acid value | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap