Cold rolling production method of medium-chromium ferrite stainless steel for vehicle exhaust system

一种汽车排气系统、生产方法的技术，应用在金属轧制、金属轧制、轧机控制装置等方向，能够解决提高制造成本、起皱和开裂、成形性不良等问题，达到降低生产成本、大剪切应变能、提高生产效率和成材率的效果

Inactive Publication Date: 2016-11-23
BAOSTEEL DESHENG STAINLESS STEEL
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Exhaust system components are prone to various wrinkles and cracks due to poor formability during the stamping production process, resulting in scrapped parts, which not only increases manufacturing costs, but also causes waste of materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The longitudinal grain structure of the cold-rolled annealed sheet of embodiment 1 is as follows figure 1 As shown, the corresponding grain size is grade 7. The grain structure of comparative example 1 is as figure 2 As shown, the grain size is 6.5.

[0044] Depend on figure 1 , figure 2 It can be seen that the steel grains produced by five continuous rolling of the present invention are smaller and more uniform than the steel grains produced by twenty-rollers of Comparative Example 1. big. Therefore, the present invention has a high recrystallization nucleation rate, finer grains after annealing, and uniform grain size in the thickness direction.

[0045] Example 1 and comparative example 1 steel plate longitudinal section shear strain after cold rolling is respectively as follows image 3 , Figure 4 shown. Depend on image 3 , 4 It can be seen that on the longitudinal section of the slab corresponding to Example 1, a shear strain ring with a large amplitu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
roughnessaaaaaaaaaa
directional tensile yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a cold rolling production method of medium-chromium ferrite stainless steel for a vehicle exhaust system. Cold rolling steps adopt five passes of continuous cold rolling by a five-stand tandem rolling unit; the reduction rate in the first pass is 19-21%; the reduction rate in the second pass is 34-36%; the reduction rate ratio in the third, fourth and fifth passes is 6-7: 4-5: 3; the total reduction rate is not lower than 70%; and the plate thickness after cold rolling is within 0.8-1.5 mm. The steel has the r value of 1.5-1.8, the yield strength of not less than 240 MPa, the tensile strength of not less than 415 MPa, the ductility of not less than 36% and the roughness of not more than 0.7 microns; the molding strain ratio of the steel is increased; the forming performance is enhanced; the roughness satisfies the use conditions of the vehicle exhaust system; and a new technology is provided for industrial production of the medium-chromium ferrite stainless steel for the vehicle exhaust system.

Description

technical field [0001] The invention belongs to the field of preparation of medium-chromium ferritic stainless steel cold-rolled plates, and in particular relates to a cold-rolled production method of medium-chromium ferritic stainless steel used in an automobile exhaust system. Background technique [0002] In recent years, with the rapid development of my country's automobile industry, the requirements for the classification of automobile emissions and the weight reduction of automobiles for energy saving have been further increased. Stainless steel materials, especially high-performance medium-chromium ferritic stainless steel materials, have been widely used, and their usage is increasing year by year, mainly for exhaust systems. [0003] The medium-chromium ferritic stainless steel used in automobile exhaust system is usually cold-rolled plate. The reciprocating cold-rolled plate developed in the 1950s is the main production method of stainless steel cold-rolled plate a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/28B21B37/00
Inventor 张志霞毕洪运李鑫刘春粟沈继程
Owner BAOSTEEL DESHENG STAINLESS STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap