Steel surface treating agent with self-repairing function

[0017] Example 1:

[0018] The present invention is a steel surface treatment agent with self-healing function. The composition and mass percentages of each component are: carrier water-based resin: 30%, anti-wear agent: 2%, sealant: 3%, and regulator : 4%, pickling accelerator: 2%, inorganic powder: 3%, stabilizer: 3%, the rest is deionized water.

[0019] The carrier water-based resin is a mixture of water-based resin, lubricating oil and nickel-iron alloy powder. The whiteness of the water-based resin, lubricating oil and nickel-iron alloy powder in the total mass of the carrier water-based resin are respectively: 35%, 50%, and 15%; and it has been activated. ; The method of activation treatment is: use polyvinylpyrrolidone steam in contact with it for 2-3h and then cool to room temperature.

[0020] The anti-wear agent is flake graphite.

[0021] The blocking agent is a blocking agent with a concentration of 10%.

[0022] The regulators are pH regulators and defoamers.

[0023] The co

[0025] Example 2:

[0026] The present invention is a steel surface treatment agent with self-repairing function. Its components and mass percentages of each component are respectively: carrier water-based resin: 45%, anti-wear agent: 5%, sealing agent: 5%, regulator : 10%, pickling accelerator: 4%, inorganic powder: 6%, stabilizer: 5%, the rest is deionized water.

[0027] The carrier water-based resin is a mixture of water-based resin, lubricating oil and nickel-iron alloy powder. The whiteness of the water-based resin, lubricating oil and nickel-iron alloy powder in the total mass of the carrier water-based resin are 52%, 30%, and 18% respectively; and it has been activated. ; The method of activation treatment is: use polyvinylpyrrolidone steam to contact with it for 3h and then cool to room temperature.

[0028] The anti-wear agent is flake graphite.

[0029] The blocking agent is a blocking agent with a concentration of 20%.

[0030] The regulators are pH regulators and defoamers.

[0033] Example 3:

[0034] The present invention is a steel surface treatment agent with self-repairing function. Its components and the mass percentages of each component are respectively: carrier water-based resin: 40%, anti-wear agent: 3%, sealing agent: 4%, regulator :7%, pickling accelerator: 3%, inorganic powder: 5%, stabilizer: 4%, the rest is deionized water.

[0035] The carrier water-based resin is a mixture of water-based resin, lubricating oil and nickel-iron alloy powder. The whiteness of the water-based resin, lubricating oil and nickel-iron alloy powder in the total mass of the carrier water-based resin are respectively: 45%, 45%, and 10%; and it has been activated. ; The method of activation treatment is: use polyvinylpyrrolidone steam to contact with it for 3h and then cool to room temperature.

[0036] The anti-wear agent is flake graphite.

[0037] The blocking agent is a blocking agent with a concentration of 20%.

[0038] The regulators are pH regulators and defoamer