Artificial granite panel and preparing method thereof
A technology of granite and granite powder, which is applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of unsatisfactory heat resistance, etc., and achieve good market application prospects, good comprehensive performance, and environmental friendliness Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0030] Example 1
[0031] Mix 500 grams of E-51 epoxy resin, 250 grams of 1,3-diglycidyl resorcinol epoxy resin, 250 grams of 3,4-epoxycyclohexanoic acid-3',4'-epoxy The cyclohexylmethyl epoxy resin was added to the reaction kettle, and after stirring and mixing evenly, 50 grams of 4,4'-diamino-4"-hydroxytriphenylmethane (DAHTM) was added, stirred and mixed, and reacted at 90°C for 1 hour, Cool to below 60°C, add 100 grams of latent curing agent LRC30, then add 300 grams of methyltetrahydrophthalic anhydride and 100 grams of dodecyl succinic anhydride, stir and mix evenly to obtain 1550 grams of DAHTM-type resin, denoted as DAHTM- 1.
Example Embodiment
[0032] Example 2
[0033] Mix 100 g CE793 epoxy resin, 300 g N,N,N',N'-tetraglycidyl-4,4'-diaminodiphenylmethane epoxy resin, 600 g diglycidyl isophthalate ring Oxygen resin was added to the reaction kettle, and after stirring and mixing evenly, 80 grams of 4,4'-diamino-4"-hydroxytriphenylmethane (DAHTM) was added, stirred and mixed, reacted at 100 °C for 1 hour, and cooled to below 60 °C , add 70 grams of latent curing agent LRC30, then add 600 grams of hexahydrophthalic anhydride, stir and mix evenly to obtain 1750 grams of DAHTM-type resin, denoted as DAHTM-2.
Example Embodiment
[0034] Example 3
[0035] 300 grams of N,N,O-triglycidyl-p-aminophenol epoxy resin, 100 grams of phenol-formaldehyde novolac type epoxy resin, 600 grams of 3,4-epoxycyclohexanoic acid-3',4' - Epoxy cyclohexylmethyl epoxy resin was added to the reaction kettle, after stirring and mixing evenly, 100 grams of 4,4'-diamino-4"-hydroxytriphenylmethane (DAHTM) was added, stirred and mixed, and reacted at 110 °C After 1 hour, cool down to below 60°C, add 50 grams of latent curing agent LRC30, then add 100 grams of hexahydrophthalic anhydride, 600 grams of tung oil anhydride and 100 grams of dodecyl succinic anhydride, stir and mix well to obtain 1950 grams of DAHTM type resin, denoted as DAHTM-3.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap