Preparation method of filtering material for adsorbing fluorine ions in water
A fluoride ion and filter material technology, applied in the field of water treatment, can solve problems such as skeletal fluorosis, and achieve the effects of easy-to-obtain raw materials, high chemical stability, and simple preparation and treatment processes
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] A method for preparing a fluoride ion adsorption filter material in water, the method comprising the following steps:
[0017] Step 1. Dissolve 1g of Al-PAM powder in 100ml of deionized water to obtain a flocculant solution with a mass fraction of 1%, and dissolve it with 1% NaOH to adjust the pH value to 10;
[0018] Step 2. Add formaldehyde to the above solution, react in a constant temperature water bath at 50°C for 1h, then slowly add diethylenetriamine (DETA) dropwise, and react for 3h, wherein the molar ratio of formaldehyde, DETA and AM is 3:2:1, Obtain a milky white solution, which is the intermediate graft product Al-PAM-DETA;
[0019] Step 3. Reduce the milky white solution obtained above to 25°C, add NaOH, add carbon disulfide dropwise at a rate of 0.1ml / min for 4 hours, raise the temperature to 55°C, and react for 2 hours, where CS 2 , The molar ratio of DETA and NaOH is 3:1:3; the product solution is obtained;
[0020] Step 4: drop the product solution int
Embodiment 2
[0027] Step 2. Add formaldehyde to the above solution, react in a constant temperature water bath at 50°C for 1h, then slowly add diethylenetriamine (DETA) dropwise, and react for 3h, wherein the molar ratio of formaldehyde, DETA and AM is 3:1:1, The milky white solution was obtained, which was the intermediate graft product Al-PAM-DETA; the rest of the steps were the same as in Example 1.
Embodiment 3
[0029] Step 2. Add formaldehyde to the above solution, react in a constant temperature water bath at 50°C for 1h, then slowly add diethylenetriamine (DETA) dropwise, and react for 3h, wherein the molar ratio of formaldehyde, DETA and AM is 1:2:1, The milky white solution was obtained, which was the intermediate graft product Al-PAM-DETA; the rest of the steps were the same as in Example 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap