Anti-aging auxiliary agent bag and preparation method thereof and application of anti-aging auxiliary agent bag in carbon fiber prepreg
A carbon fiber prepreg and anti-aging technology, which is applied in the field of special additives, can solve the problems of large precipitation risk, unsatisfactory formula design, and high-temperature curing requirements of antioxidants, and achieve good synergy and improve thermal oxygen resistance. Effects of Aging and Photoaging on Properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0029] Example 1
[0030] In this example, an anti-aging package product applied to an epoxy resin curing carbon fiber pre-leaching cloth comprises a component of the following mass percentage:
[0031] Liquid phenylene ultraviolet absorber: 60%;
[0032] Liquid light stabilizer UV-292: 30%;
[0033] Antioxidant 1076: 10%.
[0034] The anti-old aid package product was prepared by the following method:
[0035] (1) After using the liquid phenylclycopathy ultraviolet absorber and liquid light stabilizer UV-292, it is placed in a 304 stainless steel bucket to stir mixed with high mixing machine.
[0036] (2) In accordance with the above-mentioned mass percentage content, the liquid mixture obtained by the above-mentioned mass content is placed in the liquid mixture obtained by the step (1); the temperature of the stirring can increase to 80 ° C, stirred to the solid antioxidant powder completely Dissolved, the product is clear and transparent, over 400 stainless steel filters, and the t
Example Embodiment
[0037] Example 2
[0038] In this example, an anti-aging package product applied to an epoxy resin curing carbon fiber pre-leaching cloth comprises a component of the following mass percentage:
[0039] Liquid ultraviolet absorber UV-400: 45%;
[0040] Liquid light stabilizer UV-292: 40%;
[0041] Antioxidant 1076: 15%.
[0042] The anti-old aid package product was prepared by the following method:
[0043](1) After the liquid ultraviolet absorber UV-400 and the liquid light stabilizer UV-292 are priced in the 304 stainless steel bucket and mixed with high mixing machines.
[0044] (2) In accordance with the above-mentioned mass percentage content, the liquid mixture obtained by the above-mentioned mass content is placed in the liquid mixture obtained by the step (1); the temperature of the stirring can increase to 80 ° C, stirred to the solid antioxidant powder completely Dissolved, the product is clear and transparent, over 400 stainless steel filters, and the transparent liquid-li
Example Embodiment
[0045] Example 3
[0046] In this example, an anti-aging package product applied to an epoxy resin curing carbon fiber pre-leaching cloth comprises a component of the following mass percentage:
[0047] Liquid UV absorbent UV 384-2: 60%;
[0048] Liquid light stabilizer UV-292: 25%;
[0049] Antioxidant 245: 15%.
[0050] The anti-old aid package product was prepared by the following method:
[0051] (1) After the liquid ultraviolet absorber UV 384-2 and the liquid light stabilizer UV-292 are priced in the above-mentioned mass content, the mixture is placed in a 304 stainless steel barrel to stir mixture.
[0052] (2) In accordance with the above-mentioned mass percentage content, it is referred to as the liquid mixture obtained by the above-mentioned mass content; the mixing tank temperature increases to 80 ° C, stirred to the solid antioxidant powder completely Dissolved, the product is clear and transparent, over 400 stainless steel filters, and the transparent liquid-like anti-ag
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap