Method of preparing golden yellow film-coating glass or ceramic

A technology of coated glass and manufacturing method, which is applied in the field of coating material and coating, can solve the problems of expensive equipment, high production cost, complex equipment and process, etc., and achieve the effect of low equipment cost, low production cost and convenient operation

Inactive Publication Date: 2009-01-07
HUZHOU TIAHE AUTOMOBILE PART
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, ion plating or reactive sputtering plating is commonly used. The golden yellow coating on the surface of g

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The method for manufacturing golden yellow coated ceramics is to coat the nickel-chromium-titanium alloy on the ceramic surface by vacuum evaporation method, and then enter the oven for heat treatment to obtain the golden yellow coating. The specific operation is:

[0019] 1. Cleaning and drying: First, thoroughly remove the oil and other dirt on the ceramic surface. Generally, after degreasing, scrub with cleaning and deionized water, and then enter the oven or drying tunnel to dry.

[0020] 2. Vacuum evaporation: According to the size, shape and production volume of the work body, select vacuum evaporation equipment, work body frame and evaporation source (tungsten twisted wire) distribution. Now take the ceramic flat body and single tungsten stranded wire with a length of 100 mm, a width of 80 mm, and a thickness of 5 mm as an example: a titanium wire with a diameter of 0.5 mm and a nickel-chromium wire with a diameter of 0.35 mm are twisted in advance with a machine Togeth

Embodiment 2

[0024] The method for manufacturing golden coated glass is to coat the nickel-chromium-titanium alloy on the surface of the glass by vacuum evaporation method, and then enter the oven for heat treatment to obtain the golden coating. The specific operation is:

[0025] 1. Cleaning and drying: First, thoroughly remove all kinds of dirt on the glass surface. Use "fresh" float glass as much as possible (that is, float glass shortly after manufacture). Finally, rinse it with clean water and deionized water, and heat and dry it in a drying tunnel or oven.

[0026] 2. Vacuum evaporation: The basic operation is roughly the same as in the first embodiment. As another example, a double-layer membrane structure can also be used. For example, for float glass with a length of 100 mm, a width of 80 mm, and a thickness of 5 mm, the double tungsten twisted wire is used for evaporation: the 300 mm long double-stranded mixed wire in one tungsten twisted wire is evaporated, and then the other tungsten

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a golden yellow plating glass or a manufacturing method of a ceramic. The manufacturing method comprises the following steps: plating nickel-chromium-titanium alloy on the surface of the glass or the ceramic by using a vacuum vapor plating method; then entering a drying oven for heat treatment; and finally obtaining a golden yellow plating layer. The vacuum vapor plating method comprises the following steps: placing a plating material under the high vacuum condition for electrifying and heating through tungsten twisted filaments; evaporating and depositing on the surface of a body simultaneously; and then agglomerating a film. The golden yellow filming glass has the advantages of the adoption of the vacuum vapor plating method to plate the golden yellow plating layer, low cost of a device, simple process, lower production cost, convenient operation and easy maintenance and repair of the device A double stranded wire of a nickel-chromium-titanium alloy wire or a nickel chrome wire and a titanium wire is adopted as the plating material, thereby enhancing the coloring effect, in particular to better golden yellow coloring effect of the nickel chrome wire and titanium wire after being subjected to mixed vapor plating. The implementation of the heat treatment is improved by adopting the nickel-chromium-titanium alloy; the requirements on the temperature are lower; the power consumption is less; and the energy is saved.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner HUZHOU TIAHE AUTOMOBILE PART
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap