Preparing method of flame-retardant mixed silicone rubber by utilization of platinum compound and vapor-phase-method white carbon black in combination
A technology of fumed white carbon black and silicone rubber mixing, which is applied in the field of rubber products, can solve the problems of poor performance of flame retardant mixing silicone rubber, etc., and achieve the effects of good flame retardant performance, convenient preparation, and positive color
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0011] Example 1
[0012] A method for preparing flame-retardant mixed silicone rubber by using platinum compound and fumed white carbon black together. The method steps are as follows:
[0013] a. In platinic acid, add vapor-phase white carbon black with a specific surface area of 50 square meters / g, and place it at room temperature for 10 hours after mixing to form a mixture of platinum compound and white carbon black;
[0014] b. Add fumed white carbon black, modifier and iron oxide with a specific surface area of 200㎡ / g to the methyl vinyl silicone rubber raw rubber with a degree of polymerization of 7000, mix it evenly in a kneader, and heat it at 150℃2 After hours, add the flame retardant additive gas phase titanium dioxide and the mixture of platinum compound and white carbon black and mix it evenly on a two-roll rubber mixer to form a rubber compound.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap