Preparation method of mosquito compound eye-imitating hydrophobic surface material
一种表面材料、疏水材料的技术,应用在仿蚊子复眼疏水性表面材料的制备领域,能够解决操作过程复杂等问题,达到制备过程简单易操作、性能优异、降低生产成本的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment Construction
[0017] Mix acetic acid and water at a ratio of 1:10 and put it into a watering can, spray evenly on the glass surface of 10×10cm, then rinse with deionized water for 1 to 2 minutes to clean the glass; Spin-coat the photoresist on the clean glass surface, set the speed of the homogenizer to 1000-2000r / min, then move it into the oven, and dry it at 105-110°C for 10-20min, take it out and spin-coat the photoresist again, the speed remains the same It is 1000-2000r / min, and then moved into an oven, heated at 105-110°C for 20-40min to obtain a photoresist template with a thickness of 15-20μm; expose the above-mentioned photoresist template under a 900-1000W ultraviolet lamp, Then put it into a sodium hydroxide solution with a concentration of 0.3-0.5mol / L for development, then rinse it with secondary deionized water, and dry it in a high-frequency dryer. The frequency of the dryer is 10-15MHz, and the power is 2-3kW to obtain a cylindrical photoresist plate; heat the photoresist pl...
PUM
Property | Measurement | Unit |
---|---|---|
composition ratio | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap