Glaze with low surface attaching force after drying for chinaware

[0014] Example 1

[0015] A glaze for porcelain with low surface adhesion after drying, which is made of the following components by weight: 13 parts of gray calcium powder, 27 parts of Qimen kaolin, 8 parts of silica, 6 parts of spodumene, phthalocyanine 1.5 parts of blue, 1.5 parts of aventurine, 7 parts of zirconium diboride, 3 parts of magnesium sulfate powder, 5 parts of quartz sand, 2.5 parts of boron nitride, 6 parts of stabilizing additives, 8 parts of modified rutile.

[0016] The stabilizing aid is composed of the following components in parts by weight: 2.5 parts of nano aluminum hydroxide, 1.5 parts of cationic starch, 1.5 parts of boric acid, 4 parts of sodium fluorosilicate, 4 parts of glaze ash, 1.5 parts of dysprosium trioxide; The preparation method is to mix and grind the raw materials into fine powder, then treat the fine powder with 80KHz ultrasonic for 10 minutes, then mix the fine powder with 35% by weight of water and stir uniformly to form a slurry, and then se

[0021] Example 2

[0022] A glaze for porcelain with low surface adhesion after drying, which is made of the following parts by weight: 8 parts of gray calcium powder, 22 parts of Qimen kaolin, 6 parts of silica, 4 parts of spodumene, phthalocyanine 1 part of blue, 1 part of aventurine, 4 parts of zirconium diboride, 2 parts of magnesium sulfate powder, 3 parts of quartz sand, 2 parts of boron nitride, 4 parts of stabilizing aids, 5 parts of modified rutile.

[0023] The stabilizing aid is composed of the following components by weight: 2 parts of nano aluminum hydroxide, 1 part of cationic starch, 1 part of boric acid, 3 parts of sodium fluorosilicate, 3 parts of glaze ash, and 1 part of dysprosium trioxide; The preparation method is to mix and grind the raw materials into fine powder, and then treat the fine powder with 60KHz ultrasonic for 10 minutes, then mix the fine powder with 30% by weight of water and stir to form a slurry, and then send the slurry into the baking It is drie

[0028] Example 3

[0029] A porcelain glaze with low surface adhesion after drying, which is made of the following components by weight: 18 parts of gray calcium powder, 32 parts of Qimen kaolin, 10 parts of silicon dioxide, 8 parts of spodumene, phthalocyanine 2 parts of blue, 2 parts of aventurine, 10 parts of zirconium diboride, 4 parts of magnesium sulfate powder, 6 parts of quartz sand, 3 parts of boron nitride, 8 parts of stabilizing additives, 10 parts of modified rutile.

[0030] The stabilizing aid is composed of the following components in parts by weight: 3 parts of nano aluminum hydroxide, 2 parts of cationic starch, 2 parts of boric acid, 5 parts of sodium fluorosilicate, 5 parts of glaze ash, and 2 parts of dysprosium trioxide; The preparation method is to mix and grind the raw materials into fine powder, and then treat the fine powder with 100KHz ultrasonic for 10 minutes, then mix the fine powder with 40% by weight of water and stir uniformly to form a slurry, and then