Water-based UV curving vacuum electroplating finishing coating, preparation method and electroplating method thereof
A vacuum electroplating and water-based technology, applied in the field of chemical coatings, can solve the problems of poor adhesion, easy friction, scratches and scratches of metal coatings, and achieve the effect of solving poor adhesion, simple construction and good adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0046] The preparation method of waterborne UV curing vacuum electroplating topcoat provided by the present invention includes the following steps:
[0047] (1) Add the water-based acrylate, trimethylolpropane triacrylate, cosolvent, and leveling agent into the disperser according to the formula ratio and stir at 400~500r / min for 5~15min;
[0048] (2) Add the water-based polyurethane acrylate, photoinitiator, and water to the mixture in step (1) and stir at 900~1100r / min for 5~10min.
[0049] The method for electroplating water-based UV curing vacuum electroplating topcoat provided by the present invention includes the following steps:
[0050] (1) Material handling:
[0051] a) Top coat treatment: filter the top coat with a 600 mesh filter for use;
[0052] b) Pretreatment: wipe the substrate with alcohol to remove oil stains and dust on the substrate, spray primer, and the air pressure of the spray gun is 2.0~3.0kg / cm 2 , The distance between the spray gun and the coating surface is
Example Embodiment
[0056] Example 1
[0057] A water-based UV curing vacuum electroplating topcoat, which includes the following components and mass parts:
[0058] Water-based polyurethane acrylate (Hefei Polymerization Radiation 709T) 50 parts;
[0059] 25 parts of water-based acrylate (BASF 7602LV);
[0060] 3 parts of trimethylolpropane triacrylate;
[0061] Leveling agent (EFKA 3777) 1.2 parts;
[0062] Photoinitiator (phenyl bis (2.4.6-trimethylbenzoyl) phosphine oxide) 6 parts;
[0063] Cosolvent (ethylene glycol butyl ether) 18 parts;
[0064] 45 parts of water.
[0065] The preparation method of the coating includes the following steps:
[0066] (1) Add water-based acrylate, trimethylolpropane triacrylate, cosolvent, and leveling agent into the disperser according to the formula ratio and stir at 480 r / min for 12 min;
[0067] (2) Add the water-based polyurethane acrylate, photoinitiator, and water to the mixture in step (1) and stir at 950 r / min for 6 min.
Example Embodiment
[0068] Example 2
[0069] A water-based UV curing vacuum electroplating topcoat, which includes the following components and mass parts:
[0070] 30 parts of water-based polyurethane acrylate (Hefei polymerization and radiation HF800);
[0071] 15 parts of water-based acrylate (BASF 7601LV);
[0072] 7.5 parts of trimethylolpropane triacrylate;
[0073] Leveling agent (BYK 346) 0.3 parts;
[0074] Leveling agent (BYK 333) 0.5 part;
[0075] 3 parts of photoinitiator (2-hydroxy-2-methyl-1-phenyl-1-acetone);
[0076] Cosolvent (isopropanol) 12 parts;
[0077] 55 parts of water.
[0078] The preparation method of the coating includes the following steps:
[0079] (1) Add the water-based acrylate, trimethylolpropane triacrylate, cosolvent, and leveling agent into the disperser according to the formula ratio and stir at 450 r / min for 10 min;
[0080] (2) Add the water-based polyurethane acrylate, photoinitiator, and water to the mixture in step (1) and stir at a speed of 1000 r / min for 8 min.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap