Nanometer titanium dioxide dispersion emulsion and preparation process thereof
A nano-titanium dioxide and dispersing emulsion technology, which is applied in chemical instruments and methods, chemical/physical processes, physical/chemical process catalysts, etc., can solve the problems of limiting the use range of dispersion liquid, pH cannot reach neutral, and high dispersant dosage. Achieve the effect of improving the compatibility of solid-liquid interface, reducing surface tension and increasing penetration
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] 1. Weigh 2g of polyacrylic acid, 2g of sodium polyacrylate (average molecular weight 4000), and 8g of sodium hexametaphosphate, fully dissolve them in 156g of water, and add 20g of nano zinc oxide powder.
[0018] 2. Turn on the high-speed disperser, set the speed to 3000r / min, and pre-disperse for 15 minutes.
[0019] 3. Put the above solution into the nano grinder feed tank, set the grinder speed to 2000r / min, and grind for 5 hours to obtain nano zinc oxide dispersion emulsion.
[0020] 4. The D90 is 68.5nm tested by the particle size analyzer, and the photocatalytic effect is good.
Embodiment 2
[0022] 1. Weigh 2g of polyacrylic acid, 2g of sodium polyacrylate (average molecular weight 4000), and 8g of sodium hexametaphosphate, fully dissolve them in 156g of water, and add 20g of nano zinc oxide powder.
[0023] 2. Turn on the high-speed disperser, set the speed to 3000r / min, and pre-disperse for 15 minutes.
[0024] 3. Put the above solution into the nano grinder feed tank, set the grinder speed to 2000r / min, and grind for 8 hours to obtain nano zinc oxide dispersion emulsion.
[0025] 4. The D90 is 66.1nm after the particle size tester, and the photocatalytic effect is good.
Embodiment 3
[0027] 1. Weigh 2g of polyacrylic acid, 2g of sodium polyacrylate (average molecular weight 4000), and 8g of sodium hexametaphosphate, fully dissolve them in 156g of water, and add 20g of nano zinc oxide powder.
[0028] 2. Turn on the high-speed disperser, set the speed to 3000r / min, and pre-disperse for 15 minutes.
[0029] 3. Put the above solution into the nano grinder feed tank, set the grinder speed to 2500r / min, and grind for 5 hours to obtain nano zinc oxide dispersion emulsion.
[0030] 4. The D90 is 65.7nm tested by the particle size analyzer, and the photocatalytic effect is good.
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap