Nano heat insulation plate and preparation method thereof
A technology of nano-heat insulation and gas phase method, which is applied in the field of inorganic non-metallic material manufacturing, can solve the problems of the environment and the difficult disposal of insulation material waste, and achieve the effect of less material, low cost, and environmentally friendly construction
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0049] In a preferred embodiment, the preparation method of the alumina comprises the following steps:
[0050] (1) melting aluminum ingot, then feeding chlorine to generate aluminum trichloride steam;
[0051] (2) mixing the preheated inert gas with aluminum trichloride steam to obtain raw material gas;
[0052] (3) The raw material gas is sprayed through the nozzle, contacted and reacted with the water vapor mixture, and then separated from the gas and solid to obtain it.
[0053] In a preferred embodiment, the chlorine gas is dry chlorine gas.
[0054] In a preferred embodiment, the temperature of the preheated inert gas is not lower than 600°C.
[0055] In a preferred embodiment, the speed at which the raw material gas is ejected through the nozzle is not lower than 100 m / s.
[0056] In a preferred embodiment, the preheating temperature of the nozzle is not lower than 600°C.
[0057] In a preferred embodiment, the aperture of the nozzle is not particularly limited, and
Example Embodiment
[0103] Example 1
[0104] Embodiment 1 provides a nano heat insulation board, and the preparation raw materials of the nano heat insulation board, in parts by weight, include the following components: 70 parts of silicon dioxide, 20 parts of alumina, 20 parts of silicon carbide, and 15 parts of fibers parts, 20 parts of silica fume, and 15 parts of silica sol.
[0105] The silica is fumed silica; the particle size of the fumed silica is 20±10nm, and the specific surface area is 200m 2 / g, purchased from Shandong Dongyue Chemical Co., Ltd.
[0106] The preparation method of the alumina comprises the following steps:
[0107] (1) aluminum ingot is melted, and then dry chlorine gas is introduced to generate aluminum trichloride steam;
[0108] (2) mixing the inert gas preheated to 800°C with aluminum trichloride vapor to obtain raw material gas;
[0109] (3) The raw material gas is sprayed at a speed of 200m / s through a nozzle, contacted and reacted with the water vapor mi
Example Embodiment
[0117] Example 2
[0118] Embodiment 2 provides a nano heat insulation board, and the preparation raw materials of the nano heat insulation board, in parts by weight, include the following components: 10 parts of silicon dioxide, 10 parts of silicon carbide, 5 parts of fibers, and 5 parts of silica fume parts, 5 parts of silica sol.
[0119] The silica is fumed silica; the particle size of the fumed silica is 1±10nm, and the specific surface area is 150m 2 / g, purchased from Shandong Dongyue Chemical Co., Ltd.
[0120] The preparation method of the alumina comprises the following steps:
[0121] (1) aluminum ingot is melted, and then dry chlorine gas is introduced to generate aluminum trichloride steam;
[0122] (2) mixing the inert gas preheated to 800°C with aluminum trichloride vapor to obtain raw material gas;
[0123] (3) The raw material gas is sprayed at a speed of 200m / s through a nozzle, contacted and reacted with the water vapor mixture, and then separated fro
PUM
Property | Measurement | Unit |
---|---|---|
Microhardness | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap