Ultra-high performance concrete containing metakaolin and preparation method of ultra-high performance concrete
A metakaolin, ultra-high-performance technology, applied in the field of ultra-high-performance concrete and its preparation, can solve the problems of high viscosity of ultra-high-performance concrete slurry, limiting the application of ultra-high-performance concrete, and not being completely solved, and achieving the realization of The effect of large-scale production, short mixing time and low overall cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031] An ultra-high-performance concrete prepared with metakaolin powder, the components per cubic meter are as follows: 770kg of cement, 43kg of silica fume, 475kg of metakaolin powder, 1960kg of machine-made sand, 33kg of water reducing agent, and 200kg of water. The specific surface area of metakaolin is not less than 800m 2 / kg, the loss on ignition is not more than 2.5%, and the 28d activity index is not less than 115%. After the materials are ready, the above components are mixed, and after being stirred by a forced mixer for 2.5 minutes, a kind of ultra-high performance concrete prepared with metakaolin powder as described in the present invention can be obtained. The concrete has good workability and no segregation , Bleeding phenomenon. The performance and hardening properties of the concrete mixture are shown in Table 1.
Embodiment 2
[0033] An ultra-high-performance concrete prepared with metakaolin powder, the components per cubic meter are as follows: 800kg of cement, 46kg of silica fume, 450kg of metakaolin powder, 1900kg of machine-made sand, 35kg of water reducing agent, and 202kg of water. The specific surface area of metakaolin is not less than 800m 2 / kg, the loss on ignition is not more than 2.5%, and the 28d activity index is not less than 115%. After the materials are ready, the above components are mixed, and after being stirred by a forced mixer for 2.5 minutes, a kind of ultra-high performance concrete prepared with metakaolin powder as described in the present invention can be obtained. The concrete has good workability and no segregation , Bleeding phenomenon. The performance and hardening properties of the concrete mixture are shown in Table 1.
PUM
Property | Measurement | Unit |
---|---|---|
Specific surface area | aaaaa | aaaaa |
Specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap