一种生产工艺、彩手的技术,应用在钙质瓷的釉下彩手绘生产工艺领域,能够解决笔触缺陷、画面模糊、成本高等问题,达到画面立体感强、层次浓淡充分、生产成本降低的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] Embodiment 1, the underglaze color hand-painted production process of this kind of calcareous porcelain, adopts the following steps:
[0015] 1) Body porcelain shaping: The molded clay body is fired at 1100°C for 15 minutes to shrink and fix the shape of the body to make a porcelain body;
[0016] 2) Firing Xuan Porcelain: After spraying a layer of flux on the surface of the porcelain body, firing at 800°C for 15 minutes to make Xuan Porcelain. The composition of the flux is (in parts by weight): 32 parts of shell powder, 15 parts of feldspar powder, 28 parts of quartz powder, 10 parts of clay, 5 parts of magnesium oxide, 20 parts of water;
[0017] 3) Hand-painting: Use special coloring materials to create hand-painted creations on the surface of Xuan porcelain to make colored tires. When hand-painting, add water to the special coloring materials and mix thoroughly. The amount of water added is determined according to the color depth of the drawn pattern. (by weight):...
Embodiment 2
[0021] Embodiment two, the underglaze color hand-painted production process method of this kind of calcareous porcelain, adopts the following steps:
[0022] 1) Body porcelain shaping: the formed mud tire is fired at a temperature of 1280°C for 20 minutes to shrink and fix the tire shape to make a porcelain body;
[0023] 2) Firing Xuan Porcelain: After spraying a layer of flux on the surface of the porcelain body, firing at 850°C for 15-20 minutes to make Xuan Porcelain. The composition of the flux is (by weight): shell powder 35 20 parts of feldspar powder, 32 parts of quartz powder, 15 parts of clay, 10 parts of magnesium oxide, 30 parts of water;
[0024] 3) Hand-painting: Use special coloring materials to create hand-painted creations on the surface of Xuan porcelain to make colored tires. When hand-painting, add water to the special coloring materials and mix thoroughly. The amount of water added is determined according to the color depth of the drawn pattern. (by weigh...
Embodiment 3
[0028] Embodiment three, the underglaze color hand-painted production process method of this kind of calcareous porcelain, adopts the following steps:
[0029] 1) Body porcelain shaping: The molded clay body is fired at 1200°C for 18 minutes to shrink and fix the shape of the body to make a porcelain body;
[0030] 2) Firing Xuan porcelain: After spraying a layer of flux on the surface of the porcelain body, firing at a temperature of 830°C for 18 minutes to make Xuan porcelain. The composition of the flux is (by weight): 33 parts of shell powder, 17 parts of feldspar powder, 30 parts of quartz powder, 12 parts of clay, 8 parts of magnesium oxide, 25 parts of water;
[0031] 3) Hand-painting: Use special coloring materials to create hand-painted creations on the surface of Xuan porcelain to make colored tires. When hand-painting, add water to the special coloring materials and mix thoroughly. The amount of water added is determined according to the color depth of the drawn pat...
PUM
Property | Measurement | Unit |
---|---|---|
whiteness | aaaaa | aaaaa |
whiteness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap