Making method of high-corrosion-resistance air conditioner support

A production method and anti-corrosion technology, which is applied in air-conditioning systems, heating methods, space heating and ventilation, etc., can solve the problems of unstable structure, rust, undesigned placement platform of air-conditioning external units, etc., and achieve extended use life, avoiding the effect of shortening the service life

Inactive Publication Date: 2018-02-16
成都毅诚机电工程有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

This technology uses special materials called 305 Stainless Steel (SS), which helps prevent damage from water vapor or other substances that may attack it during its manufacturing process. It also prevents rust when exposed to certain environments where metal parts come into contact with eachother's surfaces over time without losing their effectiveness due to this exposure. An acidsic liquid containing strong bases like hydrochloric acid has been found effective at removing any unwanted material while maintaining good stability against erosion caused by these environmental factors. Additionally, there have been developed methods involving applying various coatings onto SS to improve durability. Overall, this technical results help prolong the lifespan of medical devices made up of such metals.

Problems solved by technology

This technical problem addressed in this patented text relates to how long it takes for new buildings without any type of decorative trim or other features that were added during construction due to corrosion issues caused by older building materials used outside air-conditioned devices (Air Condition Units).

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention will be further described below in conjunction with specific embodiments.

[0016] A method for manufacturing a highly corrosion-resistant air-conditioning bracket, characterized in that it includes the following steps:

[0017] Material selection: use 304 stainless steel plate as the blank;

[0018] Heat treatment: carry out solid solution treatment on the selected steel plate, keep the temperature at 1050 ℃ for 15 minutes, and then cool it rapidly; then carry out hot rolling and pressing of the steel plate to obtain the rough billet of the bracket, remove the scale and cool it rapidly;

[0019] Machining; finishing the rough blank of the bracket to obtain the complete shape of the bracket;

[0020] Manufacture of oxide layer: put the fabricated stent into the acid solution, soak for more than 30 minutes, and finally take it out and rinse;

[0021] Surface treatment: discharge treatment on the surface of the oxide layer to increase the surface roug

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for manufacturing a highly rust-resistant air conditioner bracket, which comprises the following steps: material selection: selecting 304 stainless steel plate as a blank; heat treatment: performing solution treatment on the selected steel plate, keeping the temperature at 1050° C. for 15 minutes, and then Rapid cooling; then hot-rolling and pressing the steel plate to obtain a rough bracket, which is rapidly cooled after removing the oxide scale; machining; finishing the rough bracket to obtain the complete shape of the bracket; making oxide layer: the prepared bracket Put it in the acid solution, soak it for more than 30 minutes, and finally take it out and rinse it; surface treatment: discharge treatment on the surface of the oxide layer to increase the surface roughness; anti-rust surface treatment: spray or roll on the surface of the oxide layer to resist corrosion paint, and spray polyurethane varnish three times on the surface of the anti-rust paint. The invention can effectively improve the anti-rust performance of the bracket and prolong the service life of the product.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner 成都毅诚机电工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap