Acidic double-color material electroplating peptizing solution and preparation method thereof
A pigment and acid technology, which is applied in the field of acid two-color electroplating solution glue and its preparation, can solve the problems of high cost and low electroplating qualification rate, achieve the improvement of qualification rate, reduce process, and promote self-aggregation and rearrangement. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1: An acidic dual-color electroplating gel solution
[0028] The acidic two-color material electroplating glue solution in this example includes the following components: 100-160 parts of water, 50-80 parts of oxalic acid, 30-40 parts of sulfamic acid, 10-20 parts of hydrogen peroxide, 6-10 parts of ethylenediaminetetraacetic acid Copies. The water is deionized water; the purity of oxalic acid, sulfamic acid and ethylenediaminetetraacetic acid is analytically pure; the hydrogen peroxide is a 60% hydrogen peroxide aqueous solution.
Example Embodiment
[0029] Example 2: An acidic dual-color electroplating gel solution
[0030] The components of the acidic two-color material electroplating gel solution in this embodiment are: 130 parts of water, 65 parts of oxalic acid, 35 parts of sulfamic acid, 15 parts of hydrogen peroxide, and 8 parts of ethylenediaminetetraacetic acid.
Example Embodiment
[0031] Example 3: Preparation method of acidic double-color electroplating gel solution
[0032] See attached figure 1 As shown, a method for preparing an acidic two-color material electroplating gel solution includes the following steps:
[0033] Step 1: Add 80-120 parts of water to the container and heat the water to 60-100°C;
[0034] Step 2: After the water temperature stabilizes, add 50-80 parts of oxalic acid and 30-40 parts of sulfamic acid, continue to heat the container, keep the temperature at 60-100℃, and stir, the stirring speed is 35-45r / min, stirring Last 30-40 minutes, get prefab one;
[0035] Step 3: Add 10-20 parts of hydrogen peroxide to preform 1, continue to stir for 20-30 minutes at a stirring speed of 60-80r / min, and heat the container in a water bath at a temperature of 30-50°C to obtain preform 2;
[0036] Step 4: Add 6-10 parts of ethylenediaminetetraacetic acid to the second preform, and add 20-40 parts of water, airtight the container, keep the container te
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap