Deep-sea fish skin collagen peptide
A technology for fish skin collagen and skin collagen, which is applied to animal/human proteins, specific peptides, connective tissue peptides, etc., can solve the problems of complicated preparation process and low collagenase hydrolysis efficiency, and achieves high extraction efficiency and simple and easy preparation method. line, the effect of small molecular weight
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0021] Example 1:
[0022] A deep-sea fish skin collagen peptide. The preparation method includes fish skin pretreatment, fish skin collagen extraction, fermentation broth preparation, fish skin collagen peptide preparation, and fish skin collagen peptide purification. The specific steps are as follows:
[0023] 1) Fish skin pretreatment: Take the cod skin as the raw material, wash the skin in ice water, cut it into pieces, then place it in a solution containing a degreasing agent, stir continuously at 180rpm for 36h, and control the material-liquid ratio The degreasing temperature is 1:20, and the degreasing temperature is 12°C. Then, the defatted fish skin is soaked in 0.05mol / L NaOH solution for 50 minutes. Finally, the soaked fish skin is repeatedly washed with water until it is neutral, and the water is drained for use. Pretreatment can remove the fat wrapped around the collagen fibers and non-collagenous proteins such as globulin and keratin, which is convenient for subsequent
Example Embodiment
[0033] Example 2:
[0034] A deep-sea fish skin collagen peptide. The preparation method includes fish skin pretreatment, fish skin collagen extraction, fermentation broth preparation, fish skin collagen peptide preparation, and fish skin collagen peptide purification. The specific steps are as follows:
[0035] 1) Fish skin pretreatment: take cod skin as raw material, wash and cut the fish skin in ice water, then place it in a mixture of isopropanol and ether with a volume ratio of 1:1.5 at a speed of 200 rpm Stir continuously for 40h, control the material-liquid ratio to 1:25, and the degreasing temperature is 12℃. Then, the defatted fish skin is soaked in 0.1mol / L NaOH solution for 50min, and finally the soaked fish skin is repeatedly washed with water until it is neutral. , Drain the water for later use;
[0036] 2) Extraction of fish skin collagen: swell the pretreated fish skin with 0.8 mol / L glacial acetic acid solution for 40 minutes, control the material-to-liquid ratio of
Example Embodiment
[0043] Example 3:
[0044] A deep-sea fish skin collagen peptide. The preparation method includes fish skin pretreatment, fish skin collagen extraction, fermentation broth preparation, fish skin collagen peptide preparation, and fish skin collagen peptide purification. The specific steps are as follows:
[0045] 1) Fish skin pretreatment: take cod skin as raw material, wash and cut the fish skin in ice water, then place it in a mixture of isopropanol and ether with a volume ratio of 1:1.2 at a speed of 180 rpm Stir continuously for 36 hours, control the material-liquid ratio to 1:23, and the degreasing temperature is 8°C. Then, the defatted fish skin is soaked in 0.08mol / L NaOH solution for 30 minutes, and finally the soaked fish skin is repeatedly washed with water until it is neutral. , Drain the water for later use;
[0046] 2) Extraction of fish skin collagen: swell the pretreated fish skin with 0.6 mol / L glacial acetic acid solution for 30 minutes, control the material-to-liqu
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap