Anti-aging SEBS modified asphalt and preparation method thereof
一种改性沥青、抗老化的技术,应用在建筑构件、建筑保温材料、建筑等方向,能够解决无法应用改性沥青、无法抑制热、氧老化等问题
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0028] Take 10 kg of Esso No. 70 asphalt with a penetration of 70, heat it to 180 ° C, and add styrene-ethylene / butylene-styrene block copolymer (Sinopec SEBS, model YH-601) (the number average molecular weight is 160,000) 0.8 kg, start the high-speed shearing machine, stir at a high speed at 400r / min for 1.5h, then add 0.3 kg of triphenyl phosphite, 0.4 kg of terpene resin, mix evenly, pass through the colloid mill, and then stir for 60 min , and finally added 0.015 kg of sulfur and stirred for 2 hours to prepare modified asphalt. The performance test results are shown in Table 1.
Embodiment 2
[0030] Take 10 kg of Esso No. 70 asphalt with a penetration of 70, heat it to 180 ° C, and add styrene-ethylene / butylene-styrene block copolymer (Sinopec SEBS, model YH-601) (the number average molecular weight is 160,000) 0.8 kg, start the high-speed shearing machine, stir at a high speed of 400r / min for 1.5h, then add 0.3 kg of triphenyl phosphite and mix evenly, pass through the colloid mill, then stir for 60 min, finally add 0.015 kg of sulfur and stir After 2 hours, the modified asphalt was prepared, and the performance test results are shown in Table 1.
Embodiment 3
[0032] Take 10 kg of Esso No. 70 asphalt with a penetration of 70, heat it to 180 ° C, and add styrene-ethylene / butylene-styrene block copolymer (Sinopec SEBS, model YH-601) (the number average molecular weight is 160,000) 0.8 kg, start the high-speed shearing machine, stir at a high speed for 1.5 h at a rotating speed of 400 r / min, then add 0.4 kg of terpene resin and mix evenly, pass through a colloid mill, then stir for 60 min, finally add 0.015 kg of sulfur and stir for 2 h, The modified asphalt was prepared, and the performance test results are shown in Table 1.
PUM
Property | Measurement | Unit |
---|---|---|
freezing point | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap