Flame-retardant optical transparent PP material and preparation method thereof
An optically transparent and flame retardant technology, applied in the field of engineering plastics, can solve the problems of high processing temperature, high cost, high energy consumption, etc., and achieve the effect of improving heat resistance shearing, accelerating crystallization rate, and increasing crystallization density
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0055] The present invention also provides a method of preparation of flame retardant optical transparent PP material, including the following steps:
[0056] S1: Place the PP raw material to dry 3-6 hours in a hot air box of 80 ° C;
[0057] S2: Treatment of the coupling agent and the heat stabilizer for 30 minutes, so that the coupling agent and the heat stabilizer reaches a diameter of 10-30 nanometers; an aerosolization increases the coupling agent and The specific surface area of the heat stabilizer, thereby increasing the contact area of the phosphorus nitrogen-based mixed flame retardant, which can increase the contact area of the PP raw material to the flame retardant, so that the PP and the flame retardant are mixed more uniform, and also Increases the molecular action between PP and flame retardants;
[0058]S3: After stirring the penetrating agent and a phosphorus nitrogen-based mixed flame retardant for 20 minutes by low speed mixing tub, the high-frequency powder c
Example Embodiment
[0061] Example 1
[0062] A flame retardant optical transparent PP material, composed of the following materials according to mass parts:
[0063] PP: 95 copies;
[0064] Phosphorus nitrogen-based hybrid flame retardant: 3 parts;
[0065] Antioxidant: 0.4 parts;
[0066] Nuclear agents: 0.2 parts;
[0067] Light stabilizer: 0.4 parts;
[0068] UV / UV: 0.2 parts;
[0069] Lubricant: 1 copy;
[0070] Heat stabilizer: 1 part;
[0071] Zeparator: 0.3 parts;
[0072] Coupled: 0.5 parts.
[0073] The embodiment of the present invention provides a method of preparing the flame retardant optical transparent PP material, comprising the steps of:
[0074] S1: Place the PP raw material to dry 3-6 hours in a hot air box of 80 ° C;
[0075] S2: Treatment of the coupling agent and the heat stabilizer for 30 minutes, so that the coupling agent and the heat stabilizer reach an aerosol shape having a diameter of 10-30 nanometers;
[0076] S3: After stirring the thorns and phosphorus nitrogen-based
Example Embodiment
[0079] Example 2
[0080] The preparation method and steps are consistent with the first embodiment, and the difference is:
[0081] A flame retardant optical transparent PP material, composed of the following materials according to mass parts:
[0082] PP: 75 copies;
[0083] Phosphorus nitrogen-based hybrid flame retardant: 3 parts;
[0084] Antioxidant: 0.8 parts;
[0085] Nuclear agents: 0.1 parts;
[0086] Light stabilizer: 0.2 parts;
[0087] UV / UV: 0.1;
[0088] Lubricant: 0.5 parts;
[0089] Heat stabilizer: 0.5 parts;
[0090] Zeparator: 0.2 parts;
[0091] Coupled: 0.2 parts.
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap