Micro-nano bubble water, preparation method thereof and mortar composition
一种微纳米气泡、中微纳米的技术,应用在建筑材料领域,能够解决微纳米气泡水稳定性差等问题,达到提高留存时间、稳定性好、提高稳定性的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0042] A preparation method of micro-nano bubble water, comprising the following steps:
[0043] The preparation of micro-nano bubble water is realized by the micro-nano bubble aerator. The raw material water is tap water, the pH value of the tap water is 7.09, the air is used as the aeration source, the air intake volume of the aeration gas is adjusted to 8L / min, and the circulating aeration time is for 5min; stand for 1h to obtain micro-nano bubbled water.
[0044] At 25°C, dynamic light scattering was used to measure the particle size of the micro-nano bubbles with a scattering angle of 90°. The measured D10 of the micro-nano bubbles in the water was 158 nm (that is, the proportion of bubbles smaller than 158 nm in size accounted for 10%) , D50 is 354nm (that is, bubbles with a particle size smaller than 354nm account for 50%), and D90 is 768nm (that is, bubbles with a particle size smaller than 768nm account for 90%).
[0045] The surface tension of the micro-nano bubble wa...
Embodiment 2
[0047] A preparation method of micro-nano bubble water, comprising the following steps:
[0048] The preparation of micro-nano bubble water is realized by a micro-nano bubble aerator. The raw material water is tap water, the pH value of the tap water is 7.09, and then aerated, using air as the aeration source, and adjusting the aeration gas intake to 10L / min, Circulating aeration time was 8min; left standing for 1.5h to obtain micro-nano bubble water.
[0049] In the micro-nano bubble water, the D10 of the micro-nano bubble is 162 nm, the D50 is 258 nm, and the D90 is 713 nm.
[0050] The surface tension of the micro-nano bubble water is 67.77 mN / m, and the bubble concentration in the micro-nano bubble water is 6.7×10 8 pcs / mL.
Embodiment 3
[0052] A preparation method of micro-nano bubble water, comprising the following steps:
[0053] The preparation of micro-nano bubble water is realized by a micro-nano bubble aerator. Tap water is selected as the raw material, and the pH value of the tap water is 7.09. Air is used as the aeration source, and the intake volume of the aeration gas is adjusted to 15L / min. for 15min; stand for 2h to obtain micro-nano bubbled water.
[0054] Measured in the water with micro-nano bubbles, the D10 of the micro-nano bubbles is 196 nm, the D50 is 387 nm, and the D90 is 795 nm.
[0055] The surface tension of the micro-nano bubble water is 71.3 mN / m, and the bubble concentration in the micro-nano bubble water is 4.8×10 8 pcs / mL.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap