The invention provides a method for producing a transparent clinker capable of being compounded with a colored glaze ceramic blank and relates to the technical field of building materials. The method comprises the following steps: taking quartz, potash feldspar, soda feldspar, calcite, soapstone, dolomite, barium carbonate, sodium carbonate, potassium carbonate, sodium borate and boracic acid, which are all 80-700kg and less than 100 meshes, and taking 100kg sodium chloride, sodium sulfate or fluorite, which is less than 100 meshes, as a clarifying agent; uniformly mixing the raw materials of the clinker, and then placing into a glass tank furnace for melting at 1520-1600 DEG C; and performing water-quenching, drying, crushing and screening on the melt material, thereby obtaining 20-200 mesh transparent clinker dry grains containing 50-70% of SiO2, 5-20% of Al2O3, 0-10% of CaO, 0-10% of MgO, 2-8% of K2O+Na2O, 0-8% of BaO, 0-8% of B2O3, 1-10% of clarifying agent and less than 0.5% of water. The method is used for producing the clinker; materials are selected within a preset component scope of the products; and the technology is standardized.