Method for preparing inorganic aromatic nano-antibacterial agent and antibacterial fabrics

[0018] Swell 1g of carbomer resin and 1g of glycerin in 800ml of deionized water, add 1ml of triethanolamine to adjust the pH value to 6.0-7.0, and form A solution; gram of silver nitrate, 0.2-0.3g of ascorbic acid, replace the oxygen in the bottle with high-purity nitrogen for 3-5 times under ultrasonic degassing, react at 60°C for 3 hours to obtain nano-silver antibacterial agent, and stabilize the polymer The dispersed nano-silver antibacterial agent is diluted with water to 50L, combined with 508G and 1200g of softener to make a finishing solution, and the 10×2.4m fabric is subjected to padding treatment, the excess rate is 65%, and the tenter drying temperature is 100-120°C to obtain antibacterial fabric.

[0020] Swell 1g of carbomer resin and 1g of glycerin in 800ml of deionized water, add 1ml of triethanolamine to adjust the pH value to 6.0-7.0, and form A solution; add 1-10g of polyvinyl alcohol and 800ml of A solution into a 1000mL three-necked flask, and add 1g of nitric acid Silver, 0.1-0.2g of ascorbic acid, replace the oxygen in the bottle with high-purity nitrogen for 3-5 times under ultrasonic degassing, react at 60°C for 3 hours, and mix the prepared polymer stably dispersed nano-silver antibacterial agent with water Diluted to 50L, combined with softener 508G 1200g to make finishing solution, 10×2.4m fabrics were subjected to padding treatment for 30-60s, with 65% excess rate, and tenter drying temperature 100-120°C to obtain antibacterial fabrics.

[0022] Swell 1g of carbomer resin and 1g of glycerin in 800ml of deionized water, add 1ml of triethanolamine to adjust the pH value to 6.0-7.0, and form A solution; gram of silver nitrate, 10-100ml of phytic acid, replace the oxygen in the bottle with high-purity nitrogen for 3-5 times under ultrasonic degassing, and react at 30°C for 3 hours, and the prepared polymer stably dispersed nano-silver antibacterial Dilute the agent to 50L with water, combine with 508G and 1200g of softener to make a finishing solution, and the 10×2.4m fabric is subjected to padding treatment for 30-60s, the excess rate is 65%, and the tenter drying temperature is 100-120°C to obtain antibacterial fabric.