Modification treatment method for coal ash for concrete
A treatment method, fly ash technology, applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of high cost, poor modification effect, complicated process, etc., and achieve low cost of use, Good economic benefit and simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] A modification treatment method of fly ash for concrete, comprising the following steps:
[0026] S1: Add fly ash to a ball mill, crush to 60 mesh, and sieve to obtain fly ash fine powder;
[0027] S2: Add the above-mentioned fly ash fine powder into a sodium phosphate solution with a mass concentration of 8% to soak, then wash the fly ash with water for 3 times, and dry the fly ash fine powder;
[0028] S3: Add the fly ash fine powder dried in step S2 into the mixer, heat to 60°C, add a mixed modifier with a weight of 3% of the fly ash and stir for 15 minutes at a stirring speed of 500r / min, The mixed modifier is composed of maleic rosin octylphenol polyoxyethylene ether diester carboxylate sodium and lauryl polyoxyethylene ether methyl silane with a mass ratio of 1:2, discharged and dried to complete Modification of fly ash.
Embodiment 2
[0030] A modification treatment method of fly ash for concrete, comprising the following steps:
[0031] S1: Add fly ash to a ball mill, crush to 40 mesh, and sieve to obtain fly ash fine powder;
[0032] S2: Add the above-mentioned fly ash fine powder into a sodium phosphate solution with a mass concentration of 10% to soak, then wash the fly ash with water for 4 times, and dry the fly ash fine powder;
[0033] S3: Add the fly ash fine powder dried in step S2 into the mixer, heat to 70°C, add a mixed modifier with a weight of 1.5% of the fly ash and stir for 10 minutes while stirring at a speed of 800r / min, The mixed modifying agent is composed of maleic rosin octylphenol polyoxyethylene ether diester carboxylate sodium and stearyl polyoxyethylene ether methyl silane with a mass ratio of 1:1, discharged, dried, and then Complete the modification of fly ash.
Embodiment 3
[0035] A modification treatment method of fly ash for concrete, comprising the following steps:
[0036] S1: Add fly ash to a ball mill, crush to 100 mesh, and sieve to obtain fly ash fine powder;
[0037] S2: Add the above-mentioned fly ash fine powder into a sodium phosphate solution with a mass concentration of 5% to soak, then wash the fly ash with water for 2 times, and dry the fly ash fine powder;
[0038] S3: Add the fly ash fine powder dried in step S2 into the mixer, heat to 60°C, add a mixed modifier with a weight of 3.0% of the fly ash and stir for 20 minutes while stirring at a speed of 1000r / min, The mixed modifying agent is composed of maleic rosin octylphenol polyoxyethylene ether diester carboxylate sodium and lauryl polyoxyethylene ether methylsilane with a mass ratio of 1:1, discharged and dried in the air. Complete the modification of fly ash.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap