Chromium-free SWRH82B high-carbon steel wire rod and production method

一种生产方法、高碳钢的技术，应用在钢铁生产制造领域，能够解决影响产品质量稳定性及生产效率、不容易生成马氏体、拉拔脆断等问题，达到促进化学成分均匀化、马氏体级别低、断丝率低的效果

Inactive Publication Date: 2022-04-26
HENAN JIYUAN IRON & STEEL (GRP) CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the φ12.5 specification SWRH82B high carbon steel wire rod is prone to the problem of brittle fracture during drawing. The main reason is that the severe Mn and Cr segregation and aggregation in the center lead to the abnormal structure of martensite in the product, which in turn leads to the release of the product. Or the problem of broken wires in the drawing stage seriously affects the quality stability and production efficiency of the product. The higher the cooling rate of the critical formation of martensite, the less likely it is to form martensite during cooling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045]A kind of chromium-free SWRH82B high-carbon steel wire rod, the composition of SWRH82B high-carbon steel wire rod includes: C: 0.805wt%, Si: 0.247wt%, Mn: 0.772wt%, P: 0.012wt%, S: 0.008wt% %, Cr: 0.059wt%, Al: ≤0.0022wt%.

[0046] A production method of SWRH82B high-carbon steel wire rod without adding chromium, comprising the following steps:

[0047] (1) A 150-ton top-bottom double-blowing converter is used to smelt raw materials. In the 150-ton top-bottom double-blowing converter, high-strength supplementary blowing method is used to control oxygen, and control elements C: (0.10-0.40) wt%, P: ≤0.010wt%, the temperature at the end of the converter is controlled at (1580-1680) °C, high-carbon ferromanganese is added during smelting, the amount of high-carbon ferromanganese added is 8.0kg / t, no high-carbon ferrochrome is added; after the converter is alloyed, The content of each element is controlled as follows: C: (0.72-0.77) wt%, Si: (0.15-0.21) wt%, Mn: (0.63-0.73) ...

Embodiment 2

[0059] A chrome-free SWRH82B high-carbon steel wire rod, the composition of the SWRH82B high-carbon steel wire rod includes: C: 0.814wt%, Si: 0.231wt%, Mn: 0.746wt%, P: 0.011wt%, S: 0.007wt% %, Cr: 0.034wt%, Al: ≤0.0028wt%.

[0060] The production method of the chromium-free SWRH82B high-carbon steel wire rod is the same as in Example 1.

Embodiment 3

[0062] A chrome-free SWRH82B high-carbon steel wire rod, the composition of the SWRH82B high-carbon steel wire rod includes: C: 0.821wt%, Si: 0.239wt%, Mn: 0.754wt%, P: 0.012wt%, S: 0.008wt% %, Cr: 0.039wt%, Al: ≤0.0020wt%.

[0063] The production method of the chromium-free SWRH82B high-carbon steel wire rod is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a chromium-free SWRH82B high-carbon steel wire rod and a production method. The wire rod comprises the following components: (0.80-0.84) wt% of C, (0.15-0.30) wt% of Si, (0.70-0.80) wt% of Mn, less than or equal to 0.015 wt% of P, less than or equal to 0.010 wt% of S, less than or equal to 0.10 wt% of Cr, less than or equal to 0.005 wt% of Al and the balance of Fe. The method comprises the following steps: (1) smelting raw materials by adopting a top-bottom combined blown converter, wherein chromium is not added during smelting; (2) refining by adopting an LF (Ladle Furnace) after smelting, wherein chromium is not added during refining; (3) carrying out continuous casting on a square billet with the size of (150mm * (150-180) mm after refining; (4) heating the steel billet after continuous casting; (5) after the steel billet is heated, high-pressure water is adopted for descaling; (6) carrying out high-speed wire rod rolling after descaling; and (7) carrying out controlled cooling by adopting a Stelmor air cooling line after rolling. According to the method, ferrochrome is not added into a converter and a refining furnace, steel billets are evenly heated, chemical component homogenization is promoted, the cooling speed before air cooling line phase change is increased to 10 DEG C / s or above from 7.5 DEG C / s, the sorbite proportion reaches 90% or above, steel billet element segregation is controlled, the martensite content and grade are reduced, and meanwhile it is guaranteed that the strength and area shrinkage of the wire rod meet the quality requirement.

Description

technical field [0001] The invention belongs to the field of steel production and manufacturing, and in particular relates to a chromium-free SWRH82B high-carbon steel wire rod and a production method. Background technique [0002] SWRH82B high-carbon steel wire rod is generally used in the production of high-strength metal products such as prestressed steel wire and steel strand. It is mainly used to make prestressed steel strand through drawing and stranding. Prestressed steel strand is widely used in bridges, In the fields of construction, water conservancy, energy and geotechnical engineering, prestressed steel strands need to have the characteristics of high strength, low relaxation and high toughness. [0003] However, the φ12.5 specification SWRH82B high carbon steel wire rod is prone to the problem of brittle fracture during drawing. The main reason is that the severe Mn and Cr segregation and aggregation in the center lead to the abnormal structure of martensite in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/18C21D8/06C22C33/06
CPCC22C38/02C22C38/04C22C38/06C22C38/18C22C33/06C21D8/065C21D2211/009C21D2211/008
Inventor 任建中杜志强白瑞娟孙林永刘俊丰贾川李合意吕金峄贾名琳
Owner HENAN JIYUAN IRON & STEEL (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap