Polyester-aramid guide bearing, thrust disc friction plate and manufacturing method thereof
A manufacturing method and thrust disc technology, which are applied to bearings, bearing components, shafts and bearings, etc., can solve the problems of polluted environment, poor wear resistance, complicated procedures, etc., and achieve good acid and alkali resistance, long service life, improved The effect of abrasion resistance and mechanical strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0039] Example 1
[0040] A polyester or aramid guide bearing and thrust plate friction sheet, characterized in that: a guide bearing 1 made of polyester or aramid and a thrust plate friction sheet 3 form a pair of friction pairs; the outside of the guide bearing 1 is a tube wall 15. A water flow groove 16 is also provided in the pipe wall 15; the thrust plate friction piece 3 and the cast iron base 4 constitute the thrust plate 2, and the thrust plate friction piece 3 is arranged on the cast iron base 4; the thickness of the guide bearing 1 The thickness of the friction sheet 3 of the thrust plate is 0.5mm.
[0041] A manufacturing method of the above-mentioned polyester and aramid guide bearing and thrust plate friction sheet is characterized in that:
[0042] The method consists of the following steps:
[0043] (1) Manufacture of guide bearing: impregnate polyester or aramid cloth with polyvinyl butyral modified phenolic resin for 2 hours, and dry it to obtain polyester or aramid res
Example Embodiment
[0049] Example 2
[0050] A polyester or aramid guide bearing and thrust plate friction sheet, characterized in that: a guide bearing 1 made of polyester or aramid and a thrust plate friction sheet 3 form a pair of friction pairs; the outside of the guide bearing 1 is a tube wall 15. A water flow groove 16 is also provided in the pipe wall 15; the thrust plate friction piece 3 and the cast iron base 4 constitute the thrust plate 2, and the thrust plate friction piece 3 is arranged on the cast iron base 4; the thickness of the guide bearing 1 The thickness of the friction piece 3 of the thrust plate is 0.8mm.
[0051] A manufacturing method of the above-mentioned polyester and aramid guide bearing and thrust plate friction sheet is characterized in that:
[0052] The method consists of the following steps:
[0053] (1) Manufacturing of guide bearing: impregnate polyester or aramid cloth with polyvinyl butyral modified phenolic resin for 5 hours, and dry it to obtain polyester or aramid r
Example Embodiment
[0059] Example 3
[0060] A polyester or aramid guide bearing and thrust plate friction sheet, characterized in that: a guide bearing 1 made of polyester or aramid and a thrust plate friction sheet 3 form a pair of friction pairs; the outside of the guide bearing 1 is a tube wall 15. A water flow groove 16 is also provided in the pipe wall 15; the thrust plate friction piece 3 and the cast iron base 4 constitute the thrust plate 2, and the thrust plate friction piece 3 is arranged on the cast iron base 4; the thickness of the guide bearing 1 The thickness of the friction piece 3 of the thrust plate is 0.6mm.
[0061] A manufacturing method of the above-mentioned polyester and aramid guide bearing and thrust plate friction sheet is characterized in that:
[0062] The method consists of the following steps:
[0063] (1) Manufacturing of guide bearing: impregnate polyester or aramid cloth with polyvinyl butyral modified phenolic resin for 3 hours, and dry it to obtain polyester or aramid r
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap