Halogen-free flame retardant polyamide hot-melt adhesive and preparation method thereof
A technology of polyamide hot melt adhesive and flame retardant polyamide, which is applied in the directions of adhesives, adhesive additives, non-polymer adhesive additives, etc. problem, to achieve the effect of good flame retardant performance and high bond strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0026] The preparation method of the above-mentioned halogen-free flame-retardant polyamide hot-melt adhesive comprises the following steps:
[0027] Step 1, raw material weighing: weigh according to the required raw material parts by weight;
[0028] Step 2, compounding of halogen-free flame retardants: Add the required flame retardants into the high-speed mixer and stir evenly;
[0029] Step 3, kneader mixing: add dimer acid type polyamide hot melt adhesive, halogen-free flame retardant, and antioxidant into the kneader, and knead evenly;
[0030] Step 4, twin-screw extrusion granulation: performing secondary mixing on the blend obtained in step 3 through a twin-screw extruder;
[0031] Step 5, cooling and pelletizing: extruding from a twin-screw extruder and pelletizing by a pelletizer to obtain halogen-free flame-retardant polyamide hot-melt adhesive pellets;
[0032] Step 6, drying and packaging: drying the halogen-free flame-retardant polyamide hot-melt adhesive obtained
preparation Embodiment 1
[0035] Weigh 100 parts of dimer acid type polyamide hot melt adhesive, 15 parts of halogen-free flame retardant and 1 part of antioxidant in parts by weight.
[0036] The halogen-free flame retardant consists of 10 parts of melamine polyphosphate (MPP) and 5 parts of ammonium polyphosphate (APP).
[0037] The antioxidant is composed of 0.5 part of tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester and 0.5 part of distearyl thiodipropionate (DSTDP). .
[0038] The preparation method is as follows:
[0039] Weigh the required raw materials according to the above amount, add the required melamine polyphosphate (MPP), ammonium polyphosphate (APP), etc. into the high-speed mixer, stir for 3 minutes, pour into the kneader, add the weighed dimer Acid-type polyamide hot-melt adhesive and antioxidant, mixed for 10 minutes, the hot-melt adhesive kneaded by the kneader is transferred to the twin-screw extruder extruder for secondary mixing, cooled and diced
preparation Embodiment 2
[0044] Weigh 100 parts of dimer acid type polyamide hot melt adhesive, 65 parts of halogen-free flame retardant and 0.3 part of antioxidant in parts by weight.
[0045] The halogen-free flame retardant is composed of 30 parts of melamine cyanurate (MCA), 15 parts of melamine polyphosphate (MPP), 15 parts of ammonium polyphosphate (APP), 4 parts of pentaerythritol, and 1 part of zinc oxide.
[0046] The antioxidant is 0.3 parts of tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]pentaerythritol ester.
[0047] The preparation method is as follows:
[0048] Weigh the required raw materials according to the above amount, add the required melamine cyanurate (MCA), melamine polyphosphate (MPP), ammonium polyphosphate (APP), pentaerythritol, zinc oxide, etc. into the high-speed mixer, stir for 3 minutes and pour Put into the kneader, add the weighed polyamide hot melt adhesive and antioxidant, knead for 10 minutes, the hot melt adhesive after the kneader kneading is transferre
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap