Anti-scratch paint protecting film and preparation method thereof
一种抗划痕、保护膜的技术,应用在薄膜/薄片状的粘合剂、胶粘剂等方向,能够解决增塑剂含量高、增塑剂析出、易划伤等问题,达到提高抗划痕性能以及拒水拒油耐酸耐碱性能、降低水解老化、延长使用寿命的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0037] A preparation method for an anti-scratch paint surface protection film, comprising the following steps:
[0038] 1) Synthesis of 3-hydroxy-2,4-bis(trifluoromethyl)-butyraldehyde;
[0039] Mix 3,3,3-trifluoropropanal and NaOH solution with a concentration of 2mol / L, the mass ratio of 3,3,3-trifluoropropanal and NaOH solution is 1:5, react, and the reaction temperature is 40°C , the reaction time is 2h, separated and purified to obtain 3-hydroxyl-2,4-bis(trifluoromethyl)-butyraldehyde, the structural formula is:
[0040]
[0041] 2) Synthesis of dialdehyde containing fluorine silicon;
[0042] The 3-hydroxy-2,4-bis(trifluoromethyl)-butyraldehyde was then combined with 1,1,3,3,5,5,7,7-octamethyl-1,7-tetrasiloxane Alkanediol was added to acetone, 3-hydroxy-2,4-bis(trifluoromethyl)-butyraldehyde and 1,1,3,3,5,5,7,7-octamethyl-1,7- The molar ratio of tetrasiloxanediol is 3:1, and the mass ratio of acetone to 1,1,3,3,5,5,7,7-octamethyl-1,7-tetrasiloxanediol is 5: 1. Rea...
Embodiment 2
[0053] A preparation method for an anti-scratch paint surface protection film, comprising the following steps:
[0054] 1) Synthesis of 3-hydroxy-2,4-bis(trifluoromethyl)-butyraldehyde;
[0055] Mix 3,3,3-trifluoropropanal and NaOH solution with a concentration of 4mol / L, the mass ratio of 3,3,3-trifluoropropanal and NaOH solution is 1:7, react, and the reaction temperature is 50°C , the reaction time is 3h, separated and purified to obtain 3-hydroxyl-2,4-bis(trifluoromethyl)-butyraldehyde, the structural formula is:
[0056]
[0057] 2) Synthesis of dialdehyde containing fluorine silicon;
[0058] 3-Hydroxy-2,4-bis(trifluoromethyl)-butyraldehyde was then combined with 1,1,3,3,5,5,7,7-octamethyl-1,7-tetrasiloxane di Alcohol added to acetone, 3-hydroxy-2,4-bis(trifluoromethyl)-butyraldehyde and 1,1,3,3,5,5,7,7-octamethyl-1,7-tetrasilyl The molar ratio of oxanediol is 4:1, the mass ratio of acetone to 1,1,3,3,5,5,7,7-octamethyl-1,7-tetrasiloxanediol is 10:1, Reaction, the...
Embodiment 3
[0069] A preparation method for an anti-scratch paint surface protection film, comprising the following steps:
[0070] 1) Synthesis of 3-hydroxy-2,4-bis(trifluoromethyl)-butyraldehyde;
[0071] Mix 3,3,3-trifluoropropanal and NaOH solution with a concentration of 3mol / L, the mass ratio of 3,3,3-trifluoropropanal and NaOH solution is 1:6, react, and the reaction temperature is 45°C , the reaction time is 2.5h, separated and purified to obtain 3-hydroxyl-2,4-bis(trifluoromethyl)-butyraldehyde, the structural formula is:
[0072]
[0073] 2) Synthesis of dialdehyde containing fluorine silicon;
[0074] 3-Hydroxy-2,4-bis(trifluoromethyl)-butyraldehyde was then combined with 1,1,3,3,5,5,7,7-octamethyl-1,7-tetrasiloxane di Alcohol added to acetone, 3-hydroxy-2,4-bis(trifluoromethyl)-butyraldehyde and 1,1,3,3,5,5,7,7-octamethyl-1,7-tetrasilyl The molar ratio of oxanediol is 3.5:1, and the mass ratio of acetone to 1,1,3,3,5,5,7,7-octamethyl-1,7-tetrasiloxanediol is 8: 1. React...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap