Polyvinyl chloride floor reinforcing agent prepared from hydrophobic precipitated silicon dioxide
A technology of precipitating silica and polyvinyl chloride, applied in the field of polyvinyl chloride floor reinforcement, can solve the problems of weak reinforcement effect and poor compatibility, and achieve improved performance, good compatibility, and enhanced load-bearing strength. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] (1) Add 5 parts of linear low density polyethylene and 4 parts of rubber powder to 8 parts of terpene resin, first heat to 100-105 ° C and mix for 10 minutes, then continue to heat to 125-130 ° C and mix for 10 minutes to obtain the material I;
[0020] (2) Add 5 parts of rice bran wax and 2 parts of petroleum coke to 4 parts of rosin glyceride, mix thoroughly, and then microwave at a microwave frequency of 2450MHz and a power of 700W for 10min, then add 15 parts of hydrophobic precipitated silica, 5 parts of Volcanic ash and 1 part of molecular sieve raw powder were mixed evenly and then microwaved for 5 minutes to obtain material II;
[0021] (3) Add material II, 3 parts of ceramic micropowder, 2 parts of superfine magnesium oxide, 1 part of asbestos wool, 1 part of sulphoaluminate cement, 0.5 part of bone char and 0.5 part of nano-zirconia to material I, mix well and add In a ball mill, ball mill to a fineness of less than 30 μm.
[0022] Preparation of hydrophobic pr
Embodiment 2
[0024] (1) Add 5 parts of linear low density polyethylene and 4 parts of rubber powder to 10 parts of terpene resin, first heat to 100-105 ° C and mix for 10 minutes, then continue to heat to 125-130 ° C and mix for 10 minutes to obtain the material I;
[0025] (2) Add 3 parts of rice bran wax and 2 parts of petroleum coke to 6 parts of rosin glyceride, mix thoroughly, and then microwave at a microwave frequency of 2450MHz and a power of 700W for 10min, then add 20 parts of hydrophobic precipitated silica, 4 parts of Volcanic ash and 2 parts of molecular sieve raw powder were mixed evenly, and then microwave treatment was continued for 5 minutes to obtain material II;
[0026] (3) Add material II, 2 parts of ceramic micropowder, 3 parts of ultrafine magnesium oxide, 2 parts of asbestos wool, 1 part of sulphoaluminate cement, 0.5 part of bone char and 0.5 part of nano-zirconia to material I, mix well and add In a ball mill, ball mill to a fineness of less than 30 μm.
[0027] Pr
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap