Surface phosphorization treatment agent of chemical pump stainless steel pump shell
A stainless steel pump and surface phosphating technology, which is applied in the coating process of metal materials, etc., can solve the problems of easy inclusion and precipitation of phosphating film, difficult cleaning of sediment, and easy falling off of phosphating film, so as to improve the efficiency of phosphating treatment, Good corrosion resistance, easy to solve the effect of inclusion and precipitation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0015] Example 1
[0016] A chemical pump stainless steel pump casing surface phosphating treatment agent, consisting of solution A and solution B;
[0017] The solution A is made of the following components in parts by weight: bismuth molybdate 1, sodium chloride 4, potassium carbonate 4, urea 1, water 80;
[0018] The solution B is made of the following components in parts by weight: 4 maleic anhydride, 8 ammonium phosphate, 1 sulfuric acid, 2 zinc dihydrogen phosphate, 0.2 acid additives, 1 potassium hypochlorite, 70 water; The agent is made of the following components in parts by weight: 4 alanine, 4 glycine, 1 citric acid.
Example Embodiment
[0019] Example 2
[0020] A chemical pump stainless steel pump casing surface phosphating treatment agent, consisting of solution A and solution B;
[0021] The solution A is made of the following components in parts by weight: bismuth molybdate 5, sodium chloride 8, potassium carbonate 8, urea 3, water 100;
[0022] The solution B is made of the following components in parts by weight: maleic anhydride 5, ammonium phosphate 10, sulfuric acid 3, zinc dihydrogen phosphate 4, acid additives 0.6, potassium hypochlorite 3, water 80; the acid additives The agent is made of the following components in parts by weight: 4 alanine, 4 glycine, 1 citric acid.
Example Embodiment
[0023] Example 3
[0024] A chemical pump stainless steel pump casing surface phosphating treatment agent, consisting of solution A and solution B;
[0025] The solution A is made of the following components in parts by weight: bismuth molybdate 3, sodium chloride 6, potassium carbonate 6, urea 2, water 90;
[0026] The solution B is made of the following components in parts by weight: 4.5 parts by weight of maleic anhydride, 9 parts ammonium phosphate, 2 parts sulfuric acid, 3 parts zinc dihydrogen phosphate, 0.4 parts of acid additives, 2 parts of potassium hypochlorite, and 75 parts of water; The agent is made of the following components in parts by weight: 4 alanine, 4 glycine, 1 citric acid.
[0027] Phosphating film performance test:
[0028] Table 1
[0029] Adhesion / MPa Brightness Total time of solution A and B treatment / min Example 1 6.44 81 10 Example 2 6.50 83 8 Example 3 6.46 82 9 Comparative example 1 4.28 65 15
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap