Solvent-free polyurethane adhesive for textiles, and preparation method thereof
A solvent-free polyurethane and adhesive technology, applied in the directions of adhesive additives, non-polymer adhesive additives, adhesives, etc., can solve the problems of difficult pollutant treatment and discharge, human harm, and high content, and can solve the problem of isocyanate-based Water absorption, good flame retardancy and good reactivity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] A preparation method of a solvent-free polyurethane adhesive for textiles, comprising the following steps:
[0021] (1) Under nitrogen protection, mix ammonium hexachloroiridate, nickel nitrate hydrate, cobalt nitrate, ethanol and propionic acid; Then reflux and stir for 50 minutes, then add the ammoniacal liquor that mass concentration is 20%; Reflux reaction 40 minutes; Then spin Evaporate the solvent to obtain a solid; sinter the solid at 500°C for 10 minutes, then calcinate at 650°C for 15 minutes, grind it and pass it through a 2000-mesh sieve, take the sieve and wash it until the aqueous solution after washing does not contain chloride ions and then dry Obtain functional fillers;
[0022] (2) Mixing mass concentration of 10% polyvinyl alcohol (the average molecular weight of polyvinyl alcohol is 4800) aqueous solution, tetraphenyl porphyrin iron, tert-butyl peroxybenzoate, stirred at 80°C for 3 hours, then rotary evaporated to remove water, then add hexamethylene di
Embodiment 2
[0027] A preparation method of a solvent-free polyurethane adhesive for textiles, comprising the following steps:
[0028] (1) Under nitrogen protection, mix ammonium hexachloroiridate, nickel nitrate hydrate, cobalt nitrate, ethanol and propionic acid; Then reflux and stir for 50 minutes, then add the ammoniacal liquor that mass concentration is 20%; Reflux reaction 40 minutes; Then spin Evaporate the solvent to obtain a solid; sinter the solid at 500°C for 10 minutes, then calcinate at 650°C for 15 minutes, grind it and pass it through a 2000-mesh sieve, take the sieve and wash it until the aqueous solution after washing does not contain chloride ions and then dry Obtain functional fillers;
[0029](2) Mixing mass concentration of 10% polyvinyl alcohol (the average molecular weight of polyvinyl alcohol is 4200) aqueous solution, tetraphenyl porphyrin iron, tert-butyl peroxybenzoate, stirring at 80°C for 3 hours, then rotary evaporation to remove water, then add hexamethylene d
Embodiment 3
[0034] A preparation method of a solvent-free polyurethane adhesive for textiles, comprising the following steps:
[0035] (1) Under nitrogen protection, mix ammonium hexachloroiridate, nickel nitrate hydrate, cobalt nitrate, ethanol and propionic acid; Then reflux and stir for 50 minutes, then add the ammoniacal liquor that mass concentration is 20%; Reflux reaction 40 minutes; Then spin Evaporate the solvent to obtain a solid; sinter the solid at 500°C for 10 minutes, then calcinate at 650°C for 15 minutes, grind it and pass it through a 2000-mesh sieve, take the sieve and wash it until the aqueous solution after washing does not contain chloride ions and then dry Obtain functional fillers;
[0036] (2) Mixing mass concentration of 10% polyvinyl alcohol (the average molecular weight of polyvinyl alcohol is 4800) aqueous solution, tetraphenyl porphyrin iron, tert-butyl peroxybenzoate, stirred at 80°C for 3 hours, then rotary evaporated to remove water, then add hexamethylene di
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap