Method for determining carbon black content of PE reclaimed material by using combustion method
一种回收料、燃烧法的技术,应用在利用燃烧进行化学分析、通过除去某种组分称量等方向,能够解决PE回收料热解过程不够彻底、PE回收料碳黑含量数据大、碳黑含量检测误差增大等问题,达到实现尽可能一致性、热解彻底、减少氧化的几率的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0028] A method for the carbon black content of PE recycled materials by combustion method, including the steps of initial weighing of PE recycled materials, pyrolysis, weighing after pyrolysis, combustion, and weighing after combustion, wherein pyrolysis is carried out at 600°C under nitrogen atmosphere , the holding time is extended to 50min, and the temperature is lowered to 450°C under the nitrogen atmosphere, then the nozzle is opened, and the combustion boat is dragged to the nozzle to cool for 5min, the atmosphere flow rate is the same as the existing detection standard, and then the combustion boat is removed Take it out of the combustion tube, cool it in a desiccator for 10-20 minutes, and weigh it; then put the combustion boat into the combustion tube, and pass air or oxygen into the combustion tube at a temperature of (600±20)°C at an appropriate flow rate , to burn the residual carbon black, take out the combustion boat from the combustion tube again, cool it in the...
Embodiment 2
[0031] A method for the carbon black content of PE recycled materials by combustion method, including the steps of initial weighing of PE recycled materials, pyrolysis, weighing after pyrolysis, burning, and weighing after burning, wherein PE recycled materials are heated in a nitrogen atmosphere at 600 ° C After pyrolysis, extend the holding time to 50 minutes, and then lower the temperature from 600°C to 400°C, and then open the nozzle to avoid partial oxidation of PE recycled materials in contact with air at a high temperature of 600°C, which will cause carbon black Content detection is not accurate.
Embodiment 3
[0033] A method for the carbon black content of PE recycled materials by combustion method, including the steps of initial weighing of PE recycled materials, pyrolysis, weighing after pyrolysis, burning, and weighing after burning. When the temperature is lowered from 850°C to 450°C, drag the combustion boat to the nozzle, cool for 5 minutes, cool to room temperature in a desiccator, and weigh it; Pass it into the combustion tube to burn the residual carbon black, take out the combustion boat from the combustion tube again, cool it in a desiccator for 10-20 minutes, and weigh it again.
[0034] Nitrogen gas is passed at the temperature of 0-850° C., so that the pyrolysis temperature condition is consistent with the pyrolysis temperature condition of the thermogravimetric analysis method.
[0035]After the above-mentioned high-temperature pyrolysis at 850°C, the temperature inside the tube is lowered to 450°C, which can avoid part of the PE recycled material being oxidized in c...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap